Since there is no report on the influence of machining depth on electron beam melting (EBM) parts, this paper investigated the role of superficial defects and machining depth in the performance of EBM made Inconel 718 (IN718) samples. Therefore, as-built EBM samples were analyzed against the shallow-machined (i.e., only removal of outer surfaces) and deep-machined (i.e., deep surface removal into the material) parts. It was shown that both as-built and shallow-machined samples had a drastically lower yield strength (970 ± 50 MPa), ultimate tensile stress (1200 ± 40 MPa), and ductility (28 ± 2%) compared to the deep-machined samples. This was since premature failure occurred due to various superficial defects. The superficial defects appeared in two levels, as (1) notches and pores on the surface and (2) irregular pores and cracks within the subsurface. Since the latter occurred down to 2 mm underneath the surface, shallow machining only exposed the subsurface defects to outer surfaces. Thus, the shallow-machined parts achieved only 68% and 8% of UTS and elongation of the deep-machined parts, respectively. This low performance occurred to be comparable to the as-built parts, which failed prematurely due to the high fraction surface voids and notches as well as the subsurface defects.

This paper develops a hybrid experimental/simulation method for the first time to assess the thermal stresses generated during electron beam melting (EBM) at high temperatures. The bending and rupture of trusses supporting Inconel 625 alloy panels at ~1050 °C are experimentally measured for various scanning strategies. The generated thermal stresses and strains are thereafter simulated using the Finite-Element Method (FEM). It is shown that the thermal stresses on the trusses may reach the material UTS without causing failure. Failure is only reached after the part experiences a certain magnitude of plastic strain (~0.33 ± 0.01 here). As the most influential factor, the plastic strain increases with the scanning length. In addition, it is shown that continuous scanning is necessary since the interrupted chessboard strategy induces cracking at the overlapping regions. Therefore, the associated thermal deformation is to be minimized using a proper layer rotation according to the part length. Although this is similar to the literature reported for selective laser melting (SLM), the effect of scanning pattern is found to differ, as no significant difference in thermal stresses/strains is observed between bidirectional and unidirectional patterns from EBM.