To address the difficulty in conducting fire tests to verify the fire-resistance limit of large one-way slabs with heavy loads in a metro, a scale fire test method is proposed based on the bearing capacity calculation of the one-way slab under fire. The scale fire test method adapted the hypothesis that the deflection of the one-way slab under fire is close to a half-sine function and the plane section hypothesis. The validity of this hypothesis is verified through fire tests and finite element simulations. The scale fire test method achieves a similar temperature field and mechanical behavior between the scaled model and full-scale model of the one-way slab. The results of the fire tests showed that the temperature field and mechanical behavior of the scaled model were consistent with those of the full-scale model, with an error in fire resistance of 4.7%. The calculation results and fire test results are essentially consistent, with an error of 6.5%, and according to the calculation of the one-way slab fire-resistance limit, the key factor affecting the fire resistance of the one-way slab under fire is the temperature of the bottom rebars. Using the scale fire test method, the size effect of the one-way slab under fire still exists, and larger slabs have a greater deformation capacity.

A water based ultra-thin fire resistive coating for steel structure was researched. The coating was coated on I40b I-beam with APP as the main flame retardant and titanium dioxide as filler. The full-scale fire resistance test was carried out according to the China standard GB 14907-2002. The results shows that the resistive of the water based steel structure fire resistive coating can reach 1.2h when the thickness is about 2mm. Related research shows that water based steel structure fire resistive coating can be used as an effective fire-resistant material for steel structure.

This study investigates the impact of fire on the cracking behavior of immersed tunnels. A reduced-scale (1:5) model of an immersed tunnel was constructed to conduct fire tests in both traffic tubes using the HCinc curve as the applied fire. Temperature field changes were carefully monitored during the test by thermocouples and infrared thermography on the outer surface of the tunnel’s ceiling. The continuous temperature field and temperature changes in the concrete cracks were recorded by infrared thermography. By integrating the temperature field distribution in concrete and the behavior of concrete cracking, an analysis of the depth of concrete cracking in the immersed tunnel under fire was conducted. The concrete cracks exceeded 150 mm at 95 min of the fire test. The results indicate that the inner concrete exposed to fire undergoes thermal expansion, leading to tensile cracking of the outer concrete. Additionally, the fire-exposed surface of the tunnel is vulnerable to cracking due to a temperature decrease. Thus, the design of fire resistance of immersed tunnels should take into consideration the potential for concrete cracking caused by thermal strain.