In the history of cellulose chemistry, hydrogen bonding has been the predominant explanation when discussing intermolecular interactions between cellulose polymers. This is the general consensus in scholarly textbooks and in many research articles, and it applies to several other biomacromolecules’ interactions as well. This rather unbalanced description of cellulose has likely impacted the development of materials based on the processing of cellulose—for example, via dissolution in various solvent systems and regeneration into solid materials, such as films and fibers, and even traditional wood fiber handling and papermaking. In this review, we take as a starting point the questioning of the general description of the nature of cellulose and cellulose interactions initiated by Professor Björn Lindman, based on generic physicochemical reasoning about surfactants and polymers. This dispute, which became known as “the Lindman hypothesis”, highlights the importance of hydrophobic interactions in cellulose systems and that cellulose is an amphiphilic polymer. This paper elaborates on Björn Lindman’s contribution to the subject, which has caused the scientific community to revisit cellulose and reconsider certain phenomena from other perspectives.

Aqueous sodium hydroxide solutions are extensively used as solvents for lignin in kraft pulping. These are also appealing systems for cellulose dissolution due to their inexpensiveness, ease to recycle and low toxicity. Cellulose dissolution occurs in a narrow concentration region and at low temperatures. Dissolution is often incomplete but additives, such as zinc oxide or urea, have been found to significantly improve cellulose dissolution. In this work, lignin was explored as a possible beneficial additive for cellulose dissolution. Lignin was found to improve cellulose dissolution in cold alkali, extending the NaOH concentration range to lower values. The regenerated cellulose material from the NaOH-lignin solvents was found to have a lower crystallinity and crystallite size than the samples prepared in the neat NaOH and NaOH-urea solvents. Beneficial lignin-cellulose interactions in solution state appear to be preserved under coagulation and regeneration, reducing the tendency of crystallization of cellulose.

Cellulose acetate butyrate (CAB) is a possible candidate, being a raw material derived from renewable resources, to replace fossil-based materials. This is due to its thermoplastic properties and the relative ease with which it could be implemented within the existing industry. With a significant amount of variation in CAB on the market today, a knowledge gap has been identified regarding the understanding of the polymer structural arrangement in films. This relates to the underlying mechanisms that regulate CAB film material properties, insights that are important in product development. In this study, commercially available CAB was investigated with XRD, SEM, AFM, and TOPEM DSC in order to obtain physicochemical information related to its micro-structural features in solvent-cast films. The film-forming ability relates mostly to the number of hydroxyl groups, and the semi-crystallinity of the films depends on the type and position of the side groups along the cellulose backbone. The appearance of signs of possible cholesteric ordering in the films could be connected to higher amounts of hydroxyl groups along the backbone that disturb the helix arrangement, while the overall order was primarily related to the butyrate substitution and secondarily related to the molecular weight of the particular CAB studied. Cold crystallization was also observed in one CAB sample.