Triboelectric nanogenerators (TENGs) have attracted increasing attention because of their excellent energy conversion efficiency, the diverse choice of materials, and their broad applications in energy harvesting devices and self‐powered sensors. New materials have been explored, including green materials, but their performances have not yet reached the level of that for fluoropolymers. Here, a high‐performance, fully green TENG (FG‐TENG) using cellulose‐based tribolayers is reported. It is shown that the FG‐TENG has an output power density of above 300 W m⁻², which is a new record for green‐material‐based TENGs. The high performance of the FG‐TENG is due to the high positive charge density of the regenerated cellulose. The FG‐TENG is stable after more than 30 000 cycles of operations in humidity of 30%–84%. This work demonstrates that high‐performance TENGs can be made using natural green materials for a broad range of applications.

In the history of cellulose chemistry, hydrogen bonding has been the predominant explanation when discussing intermolecular interactions between cellulose polymers. This is the general consensus in scholarly textbooks and in many research articles, and it applies to several other biomacromolecules’ interactions as well. This rather unbalanced description of cellulose has likely impacted the development of materials based on the processing of cellulose—for example, via dissolution in various solvent systems and regeneration into solid materials, such as films and fibers, and even traditional wood fiber handling and papermaking. In this review, we take as a starting point the questioning of the general description of the nature of cellulose and cellulose interactions initiated by Professor Björn Lindman, based on generic physicochemical reasoning about surfactants and polymers. This dispute, which became known as “the Lindman hypothesis”, highlights the importance of hydrophobic interactions in cellulose systems and that cellulose is an amphiphilic polymer. This paper elaborates on Björn Lindman’s contribution to the subject, which has caused the scientific community to revisit cellulose and reconsider certain phenomena from other perspectives.

Chitosan films with potential application in triboelectric nanogenerators (TENGs) represent a promising approach to replace non-biobased materials in these innovative devices. In the present work, chitosan with varying molecular weights (MW) and degrees of deacetylation was dissolved in aqueous acetic acid (AA) at different acid concentrations. It was observed that the MW had a greater influence on the viscosity of the solution compared to either the acid concentration or deacetylation degree. Gel formation occurred in high-MW chitosan solutions prepared with low AA concentration. Films prepared from chitosan solutions, through solvent-casting, were used to prepare TENGs. The power output of the TENGs increased with higher concentrations of AA used in the chitosan dissolution process. Similarly, the residual AA content in the dried films also increased with higher initial AA concentrations. Additionally, hot-pressing of the films significantly improves the TENG power output due to the decrease in morphological defects of the films. It was demonstrated that a good selection of the acid concentration not only facilitates the dissolution of chitosan but also plays a key role in defining the properties of the resulting solutions and films, thereby directly impacting the performance of the TENGs.

Due to the high electric conductivity and large surface area of nanographites, such as graphene and graphite nanoplatlets, these materials have gained a large interest for use in energy storage devices. However, due to the thin flake geometry, the viscosity of aqueous suspensions containing these materials is high even at low solids contents. This together with the use of high viscosity bio-based binders makes it challenging to coat in a roll-to-roll process with sufficient coating thickness. Electrode materials for commercial energy storage devices are often suspended by organic solvents at high solids contents and coated onto metal foils used as current-collectors. Another interesting approach is to coat the electrode onto the separator, to enable large-scale production of flat cell stacks. Here, we demonstrate an alternative, water-based approach that utilize slot-die coating to coat aqueous nanographite suspension with nanocellulose binder onto the paper separator, and onto the current collector as reference, in aqueous metal-free supercapacitors. The results show that the difference in device equivalent series resistance (ESR) due to interfacial resistance between electrode and current collector was much lower than expected and thus similar or lower compared to other studies with a aqueous supercapacitors. This indicates that electrode coated paper separator substrates could be a promising approach and a possible route for manufacturing of low-cost, environmentally friendly and metal-free energy storage devices.