The effect of phenolic antioxidant Irganox 1076 on the structure and gas permeation behavior of poly(1-trimethylsilyl-1-propyne) (PTMSP) was investigated. Isotropic films as well as thin film composite membranes (TFCM) from pure PTMSP and with added antioxidant (0.02 wt%) were prepared. PTMSP with antioxidant has a significantly higher thermal degradation stability in comparison to pure polymer. The thermal annealing of isotropic films of PTMSP with antioxidant was carried out at 140 °C. It revealed the stability of gas permeation properties for a minimum of up to 500 h of total heating time after a modest permeation values decrease in the first 48 h. X-ray diffraction data indicate a decrease in interchain distances during the heat treatment of isotropic films and indicate an increase in the packing density of macromolecules during thermally activated relaxation. Isotropic films and TFCMs from pure PTMSP and with antioxidant stabilizer were tested under conditions of constant O₂ and N₂ flow. The physical aging of thick and composite PTMSP membranes point out the necessity of thermal annealing for obtaining PTMSP-based membranes with predictable properties.

The effect of the stereoregularity of poly(1-trimethylsilyl-1-propyne) [PTMSP] (cis-content from 50 to 90%) on physical aging was investigated by measurement of the gas permeability. Films from pure PTMSP as well as those with the addition of the antioxidant Irganox 1076 were exposed to the air. The permeability of pure PTMSP films increases with an increase in cis-stereoregularity and correlates with an increase in interchain distances (according to X-ray analysis). For pure PTMSP films, the most significant aging (up to 50% of permeability drop) was observed for polymers with mixed microstructure, and the slowest aging (10–30% of permeability drop) was observed for polymers with cis-regular structure. For PTMSP films with added Irganox 1076, some decrease in permeability with time is also observed. The addition of Irganox 1076 to PTMSP in mixed as well as cis-enriched configurations visibly slows down aging. In the case of cis-regular PTMSP with a slow aging rate, the introduction of an antioxidant does not provide any advantages. The high stability of cis-regular PTMSP demonstrates the possibility of obtaining more stable membrane materials with the highest equilibrium state of the polymer selective layer prepared by casting solution.

The thermally activated relaxation of poly(1-trimethylsilyl-1-propyne) (PTMSP) samples of various cis-/trans-compositions (50–80% units of cis-configuration) in the presence of phenolic antioxidants of various structures was investigated. It was pointed out that polymers with a high content of cis-units exhibited greater thermal-oxidative stability due to the greater flexibility of the cis-enriched macrochains. The use of hindered phenols as antioxidants made it possible to prevent the process of thermally initiated oxidative degradation. At the same time, the most effective stabilizing agents were antioxidants with larger molecules such as Vulkanox BKF, Irganox 1010, and Irganox 1076. It was shown that the permeability coefficients of stabilized PTMSP during thermal treatment initially slightly decreased (by 20–30%), which, according to the X-ray diffraction data, was associated with an increase in the density of the macrochain packing, and during further heating remained practically unchanged. Note that for the cis-enriched samples, no signs of oxidation or decrease in the transport characteristics were observed during polymer heating for 240 h at 140 °C.