Massive production of carcinogenic fly ash waste poses severe threats to water bodies due to its disposal into drains and landfills. Fly ash can be a source of raw materials for the synthesis of adsorbents. Rag fly ash as a new class of raw materials could be a cheap source of Al and Si for the synthesis of Na-zeolites. In this work, NaOH activation, via a prefusion- and postfusion-based hydrothermal strategy, was practiced for the modification of rag fly ash into Na-zeolite. Morphology, surface porosity, chemical composition, functionality, mineral phases, and crystallinity, in conjunction with ion exchangeability of the tailored materials, were evaluated by SEM, ICP-OES, XRF, FTIR, XRD, and cation exchange capacity (CEC) techniques. Rag fly ash and the synthesized Na-zeolites were applied for the removal of Pb (II) from synthetic wastewater by varying the reaction conditions, such as initial metal ion concentration, mass of adsorbent, sorption time, and pH of the reaction medium. It was observed that Na-zeolite materials (1 g/100 mL) effectively removed up to 90–98% of Pb (II) ions from 100 mg/L synthetic solution within 30 min at pH ≈ 8. Freundlich adsorption isotherm favors the multilayer heterogeneous adsorption mechanism for the removal of Pb (II). It is reasonable to conclude that recycling of textile rag fly ash waste into value-added Na-zeolites for the treatment of industrial wastewater could be an emergent move toward achieving sustainable and green remediation.

Over the past few years, thermoelectrics have gained interest with regard to thermoelectricity interconversion. The improvement in the efficiency of the thermoelectric material at an ambient temperature is the main problem of research. In this work, silicon–germanium (SiGe) thin films, owing to superior properties such as nontoxicity, high stability, and their integrability with silicon technologies, were studied for thermoelectric applications. P-type SiGe thin films were deposited on quartz substrates by DC/RF magnetron sputtering and annealed at three different temperatures for 1 hour. Significant enhancement in the Seebeck coefficient was achieved for the sample annealed at 670 °C. A high power factor of 4.1 μWcm⁻¹K⁻² was obtained at room temperature.

This study enhances MoS₂/SnS₂ nanoparticles for SERS, functionalizing them with l-cysteine. Successful detection of E. coli demonstrates their potential as cost-effective SERS substrates for real-world applications.

Tin-based perovskite solar cells with a CuZnSn(Se_1−xS_x) HTL are optimized via SCAPS simulation. Tunable VBO enables 18.29% efficiency, with CZTSe_0.4S_0.6 showing ideal band alignment for enhanced photovoltaic performance.