Inspired by the enhanced gas-sensing performance by the one-dimensional hierarchical structure, one-dimensional hierarchical polyaniline/multi-walled carbon nanotubes (PANI/CNT) fibers were prepared. Interestingly, the simple heating changed the sensing characteristics of PANI from p-type to n-type and n-type PANI and p-type CNTs form p–n hetero junctions at the core–shell interface of hierarchical PANI/CNT composites. The p-type PANI/CNT (p-PANI/CNT) and n-type PANI/CNT (n-PANI/CNT) performed the higher sensitivity to NO₂ and NH₃, respectively. The response times of p-PANI/CNT and n-PANI/CNT to 50 ppm of NO₂ and NH₃ are only 5.2 and 1.8 s, respectively, showing the real-time response. The estimated limit of detection for NO₂ and NH₃ is as low as to 16.7 and 6.4 ppb, respectively. After three months, the responses of p-PANI/CNT and n-PANI/CNT decreased by 19.1% and 11.3%, respectively. It was found that one-dimensional hierarchical structures and the deeper charge depletion layer enhanced by structural changes of PANI contributed to the sensitive and fast responses to NH₃ and NO₂. The formation process of the hierarchical PANI/CNT fibers, p–n transition, and the enhanced gas-sensing performance were systematically analyzed. This work also predicts the development prospects of cost-effective, high-performance PANI/CNT-based sensors.

CdS nanowires (NWs) were fabricated through a facile low-temperature solvothermal method, following which CeO₂ nanoparticles were modified on the NWs. The ethanol sensing characteristics of pure CdS and decorated ones with different CeO₂ content were studied. It was found that the sensing performance of CdS was significantly improved after CeO₂ decoration. In particular, the 5 at% CeO₂/CdS composite exhibited a much higher response to 100 ppm ethanol (about 52), which was 2.6 times larger than that of pure CdS. A fast response and recovery time (less than 12 s and 3 s, respectively) were obtained as well as an excellent selectivity. These results make the CeO₂-decorated CdS NWs good candidates for ethanol sensing applications.

In this paper, the heterostructure of MoS₂/WS₂ was prepared by a hydrothermal method; the n-n heterostructure was demonstrated using TEM combined with Mott-Schottky analysis. The valence and conduction band positions were further identified by the XPS valence band spectra. The NH₃-sensing properties were assessed at room temperature by changing the mass ratio of the MoS₂ and WS₂ components. The 50 wt%-MoS₂/WS₂ sample exhibited the best performance, with a peak response of 23643% to NH₃ at a concentration of 500 ppm, a minimum detection limit of 20 ppm, and a fast recovery time of 2.6 s. Furthermore, the composites-based sensors demonstrated an excellent humidity immune property with less than one order of magnitude in the humidity range of 11–95% RH, revealing the practical application value of these sensors. These results suggest that the MoS₂/WS₂ heterojunction is an intriguing candidate for fabricating NH₃ sensors.