Nanostructured metallic materials with abundant high-angle grain boundaries exhibit high strength and good radiation resistance. While the nanoscale grains induce high strength, they also degrade tensile ductility. We show that a gradient nanostructured ferritic steel exhibits simultaneous improvement in yield strength by 36% and uniform elongation by 50% compared to the homogenously structured counterpart. In situ tension studies coupled with electron backscattered diffraction analyses reveal intricate coordinated deformation mechanisms in the gradient structures. The outermost nanolaminate grains sustain a substantial plastic strain via a profound deformation mechanism involving prominent grain reorientation. This synergistic plastic co-deformation process alters the rupture mode in the post-necking regime, thus delaying the onset of fracture. The present discovery highlights the intrinsic plasticity of nanolaminate grains and their significance in simultaneous improvement of strength and tensile ductility of structural metallic materials.

Ceramic materials with high strength and chemical inertness are widely used as engineering materials. However, the brittle nature limits their applications as fracture occurs before the onset of plastic yielding. There has been limited success despite extensive efforts to enhance the deformability of ceramics. Here we report a method for enhancing the room temperature plastic deformability of ceramics by artificially introducing abundant defects into the materials via preloading at elevated temperatures. After the preloading treatment, single crystal (SC) TiO ₂ exhibited a substantial increase in deformability, achieving 10% strain at room temperature. SC α-Al ₂ O ₃ also showed plastic deformability, 6 to 7.5% strain, by using the preloading strategy. These preinjected defects enabled the plastic deformation process of the ceramics at room temperature. These findings suggest a great potential for defect engineering in achieving plasticity in ceramics at room temperature.