This study focuses on the preparation and characterization of composite gaskets designed for the sealing of the solid oxide cell stacks operating below 700 °C. The seals were fabricated with the addition of various amounts (10–90 wt.%) of 3 mol.% yttria partially stabilized zirconia to a BaO-Al₂O₃-CaO-SiO₂ glass matrix. The sample gaskets in the form of thin frames were shaped by tape casting. The quality of the junctions between the composites and Crofer 22APU steel commonly used as an SOC interconnect was evaluated after thermal treatment of heating to 710 °C, then cooling to the working temperature of around 620 °C and then leaving them for 10h in an air atmosphere, before cooling to room temperature. The samples were also studied after 3, 5, and 10 thermal cycles to determine the changes in microstructure and to evaluate the porosity and possible crystallization of the glass phase. The compression of the seals was calculated on the basis of differences in thickness before and after thermal treatment. The influence of zirconia additions on the mechanical properties of the seals was studied. The experimental results confirmed that glass–ceramic composites are promising materials for gaskets in SOC stacks. The most beneficial properties were obtained for a composite containing 40 wt.% of YSZ.

This study investigates the influence of a magnetic field on the microstructure and properties of Al₂O₃–Ni composites fabricated via centrifugal slip casting at 1500 rpm. Al₂O₃ and Ni powders were combined with water and deflocculants, homogenized, and then cast into a porous plaster mold surrounded by Nd-Fe-B magnets. The resulting composites, sintered in a reducing atmosphere, exhibited a three-zone structure with varying Ni content due to the combined effects of the magnetic field and centrifugal force. SEM, EDX, and XRD analyses confirmed the distribution and composition of the phases. Hardness tests revealed the highest values at the outermost zone, with a gradual decrease toward the inner zones. Compression tests employing digital image correlation revealed high internal stresses and a significant improvement in compressive strength compared to non-magnetic field methods. This study confirms that magnetic field-assisted centrifugal slip casting significantly enhances the structural, hardness, and compressive strength properties of Al₂O₃–Ni composites, indicating promising potential for advanced applications.

The integration of solid oxide fuel cells (SOFCs) with biomass gasification reactors raises the possibility of solid particle contamination of the gaseous fuel entering the cell. Technical specifications from SOFC manufacturers, among other sources, claim that SOFCs do not tolerate the presence of solid particles in fuel. However, there is very limited literature on the experimental investigation of feeding SOFCs with particulate matter aerosols. In this study, a standard 5 × 5 cm anode-supported SOFC was fueled by two types of aerosols, namely, (1) inert powder of grain sizes and concentration equivalent to gasifier fly ash and (2) a real downdraft gasifier fly ash, both suspended in a gaseous fuel mixture. For reference, cells were also investigated with a dust-free fuel gas of the same composition. A straightforward negative influence of the inert powder aerosol could not be confirmed in experiments with a duration of 6 days. That said, the introduction of carbonaceous fly ash aerosol caused slow but irreversible damage to the SOFC. The degradation mechanisms were studied, and the presence of carbon-containing particles was found to clog the pores of the SOFC anode. The maximum measured power density of the SOFC equaled 855 mW/cm² (850 °C, reference fuel). Feeding inert aerosol fuel caused no rapid changes in power density. A moderate drop in performance was observed throughout the experiment. The contamination of fuel with fly ash resulted in an initial performance gain and a ca. 25% performance drop longer term (43 h of contamination). Post-mortem analysis revealed contamination on the walls of the gas channels, with some visible alumina or fly ash spots in the anode area.