This paper presents some examples of ceramic matrix composites (CMCs) reinforced with metal or intermetallic phases fabricated by powder consolidation without a liquid phase (melted metal). Composites with a complex structure, which are an advanced group of CMCs called hybrid composites, were described in contrast to conventional composites with a ceramic matrix. In advanced CMCs, their complex structures make it possible to achieve the synergistic effect of the micro- and nanoparticles of the metallic, intermetallic, and ceramic phases on the composite properties, which is not possible in conventional materials. Various combinations of substrates in the form of powder as more than one metal and ceramics with different powder sizes that are used to form hybrid composites were analyzed. The types of CMC microstructures, together with their geometrical schemas and some examples of real ceramic matrix composites, were described. The schemas of composite microstructures showed the possible location of the ceramic, metallic, or intermetallic phases in composites. A new concept of an advanced ceramic–intermetallic composite fabricated by the consolidation of pre-composite powder mixed with ceramic powder was also presented. This concept is based on the selection of substrates, two metals in the form of powder, which will form a new compound, intermetallic material, during processing. Metal powders were milled with ceramic powders to obtain a pre-composite powder consisting of intermetallic material and ceramics. In the next step, the consolidation of pre-composite powder with ceramic powder allows the creation of composites with complex microstructures. Selected examples of real particle-reinforced conventional and hybrid microstructures based on our own investigations were presented. In addition to microstructures, the properties and possible applications of CMCs were analyzed.

This work focuses on research on obtaining and characterizing Al₂O₃/ZrO₂ materials formed via slip casting method. The main emphasis in the research was placed on environmental aspects and those related to the practical use of ceramic materials. The goal was to analyze the environmental loads associated with the manufacturing of Al₂O₃/ZrO₂ composites, as well as to determine the coefficient of thermal expansion of the obtained materials, classified as technical ceramics. This parameter is crucial in terms of their practical applications in high-temperature working conditions, e.g., as parts of industrial machines. The study reports on the four series of Al₂O₃/ZrO₂ materials differing in the volume content of ZrO₂. The sintering process was preceded by thermogravimetric measurements. The fabricated and sintered materials were characterized by dilatometric study, scanning electron microscopy, X-ray diffraction, and stereological analysis. Further, life cycle assessment was supplied. Based on dilatometric tests, it was observed that Al₂O₃/ZrO₂ composites show a higher coefficient of thermal expansion than that resulting from the content of individual phases. The results of the life cycle analysis showed that the environmental loads (carbon footprint) resulting from the acquisition and processing of raw materials necessary for the production of sinters from Al₂O₃ and ZrO₂ are comparable to those associated with the production of plastic products such as polypropylene or polyvinyl chloride.

This paper focuses on the possibility of adapting the centrifugal slip casting method to obtain zirconia–alumina composite materials in the form of finished tube-shaped products. These types of products, due to their unique properties, can be utilised, for example, in the transport of aggressive substances, even in extreme temperatures or corrosive conditions. The study reports on the two series of zirconia–alumina composites differing in the content of ZrO₂—2.5 and 25 vol%. The fabricated and sintered materials were characterised using scanning electron microscopy (SEM), X-ray diffraction (XRD) and stereological analysis. Moreover, a life cycle assessment (LCA) was provided in accordance with the requirements of the ISO 14044 and EN 15805 standards. The obtained data clearly show that the centrifugal slip casting method allows obtaining samples with high density and extremely uniform distribution of the ZrO₂ phase in the alumina matrix. The stereological analysis results proved also that the addition of ZrO₂ is effective in reducing the growth of Al₂O₃ grains during the sintering process. The phase analysis carried out by means of XRD showed that during the sintering process, in the case of composites with a lower ZrO₂ content (2.5 vol%), the monoclinic to tetragonal transformation of ZrO₂ was total, while for samples containing 25 vol% ZrO₂, the monoclinic phase remained in a small amount in the final product.

The present work deals with the evaluation of the effect of ZrO₂ on the structure and selected properties of shapes obtained using the centrifugal slip casting method. The samples were made of alumina and zirconia. The applied technology made it possible to produce tubes with a high density reaching 99–100% after sintering. Very good bonding was obtained at the Al₂O₃/ZrO₂ interphase boundaries with no discernible delamination or cracks, which was confirmed by STEM observations. In the case of Al₂O₃/ZrO₂ composites containing 5 vol.% and 10 vol.% ZrO₂, the presence of equiaxial ZrO₂ grains with an average size of 0.25 µm was observed, which are distributed along the grain boundaries of Al₂O₃. At the same time, the composites exhibited a very high hardness of 22–23 GPa. Moreover, the environmental influences accompanying the sintering process were quantified. The impacts were determined using the life cycle analysis method, in the phase related to the extraction and processing of raw materials and the process of producing Al₂O₃/ZrO₂ composites. The results obtained show that the production of 1 kg of sintered composite results in greenhouse gas emissions of 2.24–2.9 kg CO₂ eq. which is comparable to the amount of emissions accompanying the production of 1 kg of Polyvinyl Chloride (PVC), Polypropylene (PP), or hot-rolled steel products.

In this study, ceramic–metal composites in the Al₂O₃/Ti/Ni system were fabricated using the slip casting method. Two series of composites with 15 vol.% metal content and different solid phase contents were obtained and examined. A proper fabrication process allows obtaining composites enhanced by intermetallic phases. The microstructure of the base powders, slurries, and sintered composites was analyzed by scanning electron microscope. Analysis of the sedimentation tendency of slurries was carried out. The phase composition of the sintered samples was examined by X-ray diffraction analysis. A monotonic compression test was used to investigate the mechanical properties of the composites. A fractography investigation was also carried out. The research conducted revealed that the slip casting method allows the obtaining of composites enhanced by intermetallic phases (TiNi, Ni₃Ti). The results show the correlation between solid-phase content, microstructure, and mechanical properties of the composites.

The paper describes an investigation of Al₂O₃ samples and NiAl–Al₂O₃ composites consolidated by pulse plasma sintering (PPS). In the experiment, several methods were used to determine the properties and microstructure of the raw Al₂O₃ powder, NiAl–Al₂O₃ powder after mechanical alloying, and samples obtained via the PPS. The microstructural investigation of the alumina and composite properties involves scanning electron microscopy (SEM) analysis and X-ray diffraction (XRD). The relative densities were investigated with helium pycnometer and Archimedes method measurements. Microhardness analysis with fracture toughness (K_IC) measures was applied to estimate the mechanical properties of the investigated materials. Using the PPS technique allows the production of bulk Al₂O₃ samples and intermetallic ceramic composites from the NiAl–Al₂O₃ system. To produce by PPS method the NiAl–Al₂O₃ bulk materials initially, the composite powder NiAl–Al₂O₃ was obtained by mechanical alloying. As initial powders, Ni, Al, and Al₂O₃ were used. After the PPS process, the final composite materials consist of two phases: Al₂O₃ located within the NiAl matrix. The intermetallic ceramic composites have relative densities: for composites with 10 wt.% Al₂O₃ 97.9% and samples containing 20 wt.% Al₂O₃ close to 100%. The hardness of both composites is equal to 5.8 GPa. Moreover, after PPS consolidation, NiAl–Al₂O₃ composites were characterized by high plasticity. The presented results are promising for the subsequent study of consolidation composite NiAl–Al₂O₃ powder with various initial contributions of ceramics (Al₂O₃) and a mixture of intermetallic–ceramic composite powders with the addition of ceramics to fabricate composites with complex microstructures and properties. In composites with complex microstructures that belong to the new class of composites, in particular, the synergistic effect of various mechanisms of improving the fracture toughness will be operated.