The properties of a material depend upon its physical characteristics, one of these being its crystalline state. Next generation solid-state technologies will integrate crystalline oxides into thermal sensitive processes and composite materials. Crystallization of amorphous phases of metal oxides in the solid state typically requires substantial energy input to induce the amorphous to crystalline phase transformation. In the case of silica, the transformation to α-quartz in a furnace occurs above 1300 °C and that of titania, above 400 °C. These calcination processes are costly in energy but also often degrade complex material architectures or compositions. Thus, low temperature crystallization techniques are required that preserve macro- and mesostructures and complex elemental composition (e.g., organic-, metal-, and semiconductor-metal oxide hybrids/composites). Some solution-based techniques exist to directly fabricate crystalline metal oxides. However, these are not always compatible with the specificities of the system or industrial constraints. A postsynthetic, solid-state approach that reduces crystallization temperature in metal oxides is metal-induced crystallization (MIC). MIC is the introduction of catalytic amounts of a cation, which can be an s-block, p-block, or d-block cation, that migrates through the solid metal oxide lattice. The cation is thought to temporarily break metal oxide bonds, allowing [MO_x] polyhedra to rotate and reform bonds with neighboring [MO_x] groups in a lower energy crystalline phase. Depending on the system, the cation can favor or defavor the formation of a particular crystalline phase, providing a means to tune the purity and crystalline phase ratios. An advantage of MIC is that, although the crystallization occurs in the solid state, the crystallization process can be accomplished for particle suspensions in liquid media. In this case, the energy required to induce the crystallization can come from, for example, a microwave or an ultrasound bath. The crystallization of particles in suspension avoids aggregation from particle–particle sintering. In the case of thin films, the energy for crystallization typically comes from a laser or calcination. MIC is only recently being used as a low temperature metal oxide crystallization technique, despite being widely used in the semiconductor industry. Here, the mechanism and previous studies in MIC are presented for titania, silica, and other oxides. The beauty of this technique is that it is extremely easy to employ: cations can be incorporated into the system postsynthetically and then are often expelled from the lattice upon phase conversion. We expect MIC to enrich materials for photochromic, optoelectronic, catalyst, biological, and other applications.

One can nowadays readily generate monodisperse colloidal nanocrystals, but the underlying mechanism of nucleation and growth is still a matter of intense debate. Here, we combine X-ray pair distribution function (PDF) analysis, small-angle X-ray scattering (SAXS), nuclear magnetic resonance (NMR), and transmission electron microscopy (TEM) to investigate the nucleation and growth of zirconia nanocrystals from zirconium chloride and zirconium isopropoxide at 340 °C, in the presence of surfactant (tri-n-octylphosphine oxide). Through E1 elimination, precursor conversion leads to the formation of small amorphous particles (less than 2 nm in diameter). Over the course of the reaction, the total particle concentration decreases while the concentration of nanocrystals stays constant after a sudden increase (nucleation). Kinetic modeling suggests that amorphous particles nucleate into nanocrystals through a second order process and they are also the source of nanocrystal growth. There is no evidence for a soluble monomer. The nonclassical nucleation is related to a precursor decomposition rate that is an order of magnitude higher than the observed crystallization rate. Using different zirconium precursors (e.g., ZrBr₄ or Zr(OtBu)₄), we can tune the precursor decomposition rate and thus control the nanocrystal size. We expect these findings to help researchers in the further development of colloidal syntheses.

We describe a new approach to making ultrathin Ag nanoshells with a higher level of extinction in the infrared than in the visible. The combination of near-infrared active ultrathin nanoshells with their isotropic optical properties is of interest for energy-saving applications. For such applications, the morphology must be precisely controlled, since the optical response is sensitive to nanometer-scale variations. To achieve this precision, we use a multi-step, reproducible, colloidal chemical synthesis. It includes the reduction of Tollens’ reactant onto Sn²⁺-sensitized silica particles, followed by silver-nitrate reduction by formaldehyde and ammonia. The smooth shells are about 10 nm thick, on average, and have different morphologies: continuous, percolated, and patchy, depending on the quantity of the silver nitrate used. The shell-formation mechanism, studied by optical spectroscopy and high-resolution microscopy, seems to consist of two steps: the formation of very thin and flat patches, followed by their guided regrowth around the silica particle, which is favored by a high reaction rate. The optical and thermal properties of the core-shell particles, embedded in a transparent poly(vinylpyrrolidone) film on a glass substrate, were also investigated. We found that the Ag-nanoshell films can convert 30% of the power of incident near-infrared light into heat, making them very suitable in window glazing for radiative screening from solar light.

Meta-atoms interact with light in interesting ways and offer a large range of exciting properties. They exhibit optical properties inaccessible by natural atoms but their fabrication is notoriously difficult because of the precision required. In this perspective, we present the current research landscape in making meta-atoms, with a focus on the most promising self-assembly approaches and main challenges to overcome, for the development of materials with novel properties at optical frequencies.