This study evaluated the cytotoxicity and biocompatibility of a new bioceramic endodontic sealer (i.e., Sealer Plus BC) in comparison with those of MTA Fillapex and AH Plus. L929 fibroblasts were cultured and Alamar Blue was used to evaluate cell viability of diluted extracts (1:50, 1:100, and 1:200) from each sealer at 24 h. Polyethylene tubes that were filled with material or empty (as a control) were implanted in the subcutaneous tissue of rats. The rats were killed after 7 and 30 d (n = 8), and the tubes were removed for histological analysis. Parametric data was analyzed using a one-way ANOVA test, and nonparametric data was analyzed via the Kruskal–Wallis test followed by the Dunn test (p < 0.05). A reduction in cell viability was observed in the extracts that were more diluted for Sealer Plus BC when compared to that of Control and AH Plus (p < 0.05). However, the 1:50 dilution of the Sealer Plus BC was similar to that of the Control (p > 0.05). Conversely, more diluted extracts of MTA Fillapex (1:200) and AH Plus (1:100 and 1:200) were similar to the Control (p > 0.05). Histological analysis performed at 7 d did not indicate any significant difference between tissue response for all materials, and the fibrous capsule was thick (p > 0.05). At 30 d, Sealer Plus BC was similar to the Control (p > 0.05) and MTA Fillapex and AH Plus exhibited greater inflammation than the Control (p < 0.05). The fibrous capsule was thin for the Control and for most specimens of Sealer Plus BC and AH Plus. Thus, Sealer Plus BC is biocompatible when compared to MTA Fillapex and AH Plus, and it is less cytotoxic when less-diluted extracts are used.

Injectable biomaterials, such as thermosensitive chitosan (CH)-based hydrogels, present a highly translational potential in dentistry due to their minimally invasive application, adaptability to irregular defects/shapes, and ability to carry therapeutic drugs. This work explores the incorporation of azithromycin (AZI) into thermosensitive CH hydrogels for use as an intracanal medication in regenerative endodontic procedures (REPs). The morphological and chemical characteristics of the hydrogel were assessed by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and Fourier transform infrared spectroscopy (FTIR). The thermosensitivity, gelation kinetics, compressive strength, cytocompatibility, and antibacterial efficacy were evaluated according to well-established protocols. An in vivo model of periapical disease and evoked bleeding in rats' immature permanent teeth was performed to determine disinfection, tissue repair, and root formation. AZI was successfully incorporated into interconnected porous CH hydrogels, which retained their thermosensitivity. The mechanical and rheological findings indicated that adding AZI did not adversely affect the hydrogels’ strength and injectability. Incorporating 3 % and 5 % AZI into the hydrogels led to minimal cytotoxic effects compared to higher concentrations while enhancing the antibacterial response against endodontic bacteria. AZI-laden hydrogel significantly decreased E. faecalis biofilm compared to the controls. Regarding tissue response, the 3 % AZI-laden hydrogel improved mineralized tissue formation and vascularization compared to untreated teeth and those treated with double antibiotic paste. Our findings demonstrate that adding 3 % AZI into CH hydrogels ablates infection and supports neotissue formation in vivo when applied to a clinically relevant model of regenerative endodontics.