Vulcanization is an important step in the manufacture of solid tires in which the crosslinking process occurs. In vulcanization, the materials commonly used as activators and coactivators are ZnO and stearic acid, respectively. In this research, ZnO and stearic acid were replaced with zinc stearate to improve the characteristics of vulcanized rubber. Zinc stearate was applied in four formulas with a composition of 5 to 9 phr. A formula that is often used in the rubber industry was used as a comparison, and ZnO and stearic acid of 5 phr and 2.5 phr, respectively, were applied. The rubber compound for solid tire production was developed using an open mill at a compounding temperature of 45 °C ± 5 °C. The vulcanization process of developing the rubber compound into vulcanized rubber was carried out at 150 °C for 20 min. Rubber compound test results showed that the use of zinc stearate at a ratio of 8 phr accelerated the curing time (t₉₀) between 58.3% and 69%, the scorch time (ts2) between 22.4% and 95.5%, and the torque delta (Δ_s) between 17.67 and 24.21 kg-cm. In addition, the vulcanized rubber mechanical properties test results for the compression set parameter increased between 28.6% and 57.1%. Scan results with SEM–EDS showed that using ZS could improve the homogeneous distribution of the material in the vulcanized matrix of solid tire rubber.

Synthesis of glycerol mono-laurate (GML) has been performed using esterification reaction of glycerol and lauric acid. The reaction was performed at the condition of temperature of 120–140 °C within 7 hour, variation of molar ratio of glycerol - lauric acid, and was using heterogeneous catalyst of zeolist Y. Without catalyst dealumination the maximum acid conversion was 78%, with GML contained in the sample was 38.6%, and it was obtained at the reaction condition of 140 oC, 15wt% catalyst, and 8:1 molar ratio of glycerol - lauric acid. At the same condition, using dealuminated catalyst, the maximum acid conversion was increased up to 98%, with GML contained in the sample was 50.4%. The GML antibacterial activity was examined. It was observed that the GML has antibacterial activity against gram positive bacterial such as B. cereus and S. aureus.