By enhancing the thermal properties of cement-based building materials, energy consumption and carbon dioxide (CO₂) emissions related to space conditioning in buildings can be alleviated. This study aims to present cement-based composites reinforced by textile fibers for application in building and construction. Several lightweight coating mortars were produced by partially replacing the sand in the mix with different percentages of textile waste. Mechanical and thermal characterizations of the reinforced cementitious composites were performed. The results showed that the thermal conductivity of cementitious compounds decreased as the proportion of reinforcing material in the mixture increased. In terms of mechanical properties, the textile slightly reduced the compressive strength of cementitious mortar, while it improved the flexural strength. A numerical study was then performed to derive the actual impact of these reinforced materials on the thermal behavior of a building element using COMSOL Multiphysics. Numerous configurations of walls coated with different mortar mixtures were studied. The results showed that coating both sides of a building wall with 20 mm of textile-reinforced mortar reduced the internal temperature by 1.5 °C. Thus, the application of these thermally improved mortars as coating mortars appears to be a relevant solution to enhance the thermal performance of buildings.

Faced with the growing demand for energy-efficient construction and the need to address environmental challenges, the building sector must innovate to reduce energy consumption and promote sustainability. This study investigates a dual solution to these challenges by enhancing the thermo-mechanical performance of building materials through the integration of textile fiber waste, using a combination of experimental and computational methodologies. This investigation focused on incorporating textile fiber wastes in cementitious composites for construction applications. A series of mechanical and thermal tests were carried out on the cement mortars with different proportions of incorporated textile fibers after 7 and 28 days of water curing. The results showed that the incorporation of fibers can significantly improve the thermal insulation of buildings by reducing the thermal conductivity of cement mortar by up to 52%. To complement experimental findings, computational models were developed using COMSOL Multiphysics 6.2 software to predict the thermal diffusivity and volumetric heat capacity of textile-reinforced mortars. These models revealed that mortars incorporating 40% textile fibers as a sand replacement achieved significant reductions in thermal conductivity, thermal diffusivity, and volumetric heat capacity by approximately 40%, 21%, and 23%, respectively, compared with ordinary cement mortar. Furthermore, this study numerically examined the potential of combining textile-reinforced mortar with phase-change material (PCM) in building applications. The aim of the research was to overcome the challenges of cooling buildings in scorching summer conditions. The optimization of roof and wall composition was based on an assessment of air temperature variation within a space.

Parabolic trough power plants are a promising option to produce electricity from renewable energy sources and for supplying steam to industrial processes. In this paper a parabolic trough concentrator with aperture area of 10.8 m² was designed, manufactured and evaluated in the Research and Technology Center of Energy (CRTEn) in Tunisia. Climatic conditions, concentrated solar flux and thermal efficiency of parabolic trough concentrator were recorded experimentally in June 2016. As result, the thermal efficiency reaches a maximum value of the order of 30%.