TiO₂/TeO₂ powders were obtained by an aqueous sol-gel method. Telluric acid (H₆TeO₆) and titanium butoxide were used as precursors. The as-prepared gel was step-wisely heated in the temperature range 200–700 °C and subsequently characterized by XRD, IR, and UV-Vis analysis and SEM. Mixtures containing TiO₂ (anatase), α-TeO₂ (paratellurite), and TiTe₃O₈ were established by XRD as final products, depending on heating temperature. The thermal stability of the obtained gels in the temperature range 100–400 °C was investigated. It was found by IR spectroscopy that the samples heated up to 300–400 °C consist mainly of an organic–inorganic amorphous phase which is transformed into an inorganic one above these temperatures. The microstructure of the gels was verified by scanning electron microscopy (SEM). The photocatalytic degradation of the synthesized nanopowders toward Malachite green organic dye (MG) was examined in order to evaluate the potential applications for environmental remediation. The prepared TiO₂/TeO₂ samples showed up to 60% decoloration efficiency after 120 min exposure to UV-light. The composition exhibited good antimicrobial activity against E. coli K12. The properties of the obtained material were investigated by the reactions of complete catalytic oxidation of different alkanes and toluene, and it could be suggested that TiO₂/TeO₂ powders are promising material for use as an active phase in environmental catalysts.

The current study aims to synthesize and analyze both pure and La-doped TiO₂, and evaluate the photocatalytic and antibacterial activity of as-prepared samples. Doped and undoped samples were prepared by the non-hydrolytic sol–gel method from titanium(IV) chloride, benzyl alcohol, and lanthanum(III) nitrate followed by thermal treatment. Lanthanum content in synthesized samples was 0.4, 1, and 5 mol%. The resulting nanopowders’ structure and morphology were described using XRD, IR, and UV–Vis analysis. The average particle sizes of pure and doped TiO₂ were about 6–15 nm and anatase was found to be a dominant crystalline phase in the samples. It was observed that particle sizes decreased on increasing La content. The photocatalytic activity of the pure and La-doped sol–gel powders was estimated in the decomposition of paracetamol in distilled water using ultraviolet light illumination. Doping with lanthanum ions has been shown to increase the photocatalytic properties on the degradation of paracetamol. Furthermore, the annealed catalysts (pure and La³⁺ doped) showed increased photocatalytic activity and degradation of the analgesic in comparison with non-annealed materials. In both cases, the highest photocatalytic efficiency is observed at the optimal La³⁺ (1 mol%) concentration. The antimicrobial activity of 1 mol% La/TiO₂ was tested against a reference strain E. coli in the presence of ultraviolet light and in dark conditions. The number of viable bacterial cells was determined by a spread plate method, and kill curves were performed. The results showed that photoactivated 1 mol% La/TiO₂ exhibited a strong bactericidal effect, and in concentration, 1 mg/mL efficiently killed bacteria at an initial cell density of about 10⁵ colony forming units in 1 mL within 15 min.

TiO₂ nanopowders modified by Nd and Sm were prepared using the sol-gel technique. It was found by XRD analysis that the samples containing Sm are amorphous up to 300 °C, while those with Nd preserve a mixed organic-inorganic amorphous structure at higher temperatures (400 °C). The TiO₂ (rutile) was not detected up to 700 °C in the presence of both modified oxides. TiO₂ (anatase) crystals found at about 400 °C in the Sm-modified sample exhibited an average crystallite size of about 25–30 nm, while doping with Nd resulted in particles of a lower size—5–10 nm. It was established by DTA that organic decomposition is accompanied by significant weight loss occurring in the temperature range 240–350 °C. Photocatalytic tests showed that the samples heated at 500 °C possess photocatalytic activity under UV irradiation toward Malachite green organic dye. Selected compositions exhibited good antimicrobial activity against E. coli K12 and B. subtilis.

This paper studies the influence of B₂O₃ on the structure, properties and antibacterial abilities of sol-gel-derived TiO₂/TeO₂/B₂O₃ powders. Titanium(IV) butoxide, telluric(VI) acid and boric acid were used as precursors. Differences were observed in the degree of decomposition of Ti butoxide in the presence of H₃BO₃ and H₆TeO₆ acids. The phase transformations of the obtained gels in the temperature range of 200–700 °C were investigated by XRD. Composite materials containing an amorphous phase and different crystalline phases (metallic Te, α-TeO₂, anatase, rutile and TiTe₃O₈) were prepared. Heating at 400 °C indicated a crystalline-to-amorphous-phase ratio of approximately 3:1. The scanning electron microscopy (SEM) analysis showed the preparation of plate-like TiO₂ nanoparticles. The IR results showed that the short-range order of the amorphous phases that are part of the composite materials consists of TiO₆, BO₃, BO₄ and TeO₄ structural units. Free B₂O₃ was not detected in the investigated compositions which could be related to the better connectivity between the building units as compared to binary TiO₂/B₂O₃ compositions. The UV-Vis spectra of the investigated gels exhibited a red shift of the cut-off due to the presence of boron and tellurium units. The binary sample achieved the maximum photodegradation efficiency (94%) toward Malachite green dye under UV irradiation, whereas the ternary sample photoactivity was very low. The compositions exhibited promising antibacterial activity against E. coli NBIMCC K12 407.

α-Bi2Mo3O12 and β-Bi2Mo2O9 crystal phases have been synthesized by crystallization of a glass for a short time. Amorphous samples with the compositions corresponding to the alpha and beta bismuth molybdates have been obtained at high cooling rates (104-105 K/s). XRD, DTA and SEM studies were performed to examine the phase formation, thermal behavior of the glasses and the microstructure of obtained crystalline products. By scanning electron microscopy it was shown that the obtained bismuth molybdates consist of dense agglomerates, containing uniform distributed crystals with submicron size.

Quantification of Elastin, Collagen and Advanced Glycation End Products as Functions of Age and Hypertension | InTechOpen, Published on: 2012-02-29. Authors: Milena Atanasova, Aneliya Dimitrova, Boryana Ruseva, et