TiO₂ nanopowders modified by Nd and Sm were prepared using the sol-gel technique. It was found by XRD analysis that the samples containing Sm are amorphous up to 300 °C, while those with Nd preserve a mixed organic-inorganic amorphous structure at higher temperatures (400 °C). The TiO₂ (rutile) was not detected up to 700 °C in the presence of both modified oxides. TiO₂ (anatase) crystals found at about 400 °C in the Sm-modified sample exhibited an average crystallite size of about 25–30 nm, while doping with Nd resulted in particles of a lower size—5–10 nm. It was established by DTA that organic decomposition is accompanied by significant weight loss occurring in the temperature range 240–350 °C. Photocatalytic tests showed that the samples heated at 500 °C possess photocatalytic activity under UV irradiation toward Malachite green organic dye. Selected compositions exhibited good antimicrobial activity against E. coli K12 and B. subtilis.

This study aimed to present the differences in the corrosion properties and protective ability of two bi-layer systems obtained on low-carbon steel in a model corrosive medium of 5% NaCl solution. These newly developed systems consist of Zn-Co (3 wt.%) or Zn-Ni (10 wt.%) alloy coatings as under-layers and a very thin TiO₂ sol-gel film as a top-layer. Scanning electron microscopy (SEM) is used for characterization of the surface morphology of the samples indicating that some quantitative differences appear as a result of the different composition of both zinc alloys. Surface topography is investigated by means of atomic force microscopy (AFM), and the hydrophobic properties are studied by contact angle (CA) measurements. These investigations demonstrate that both sample types possess grain nanometric surface morphology and that the contact angle decreases very slightly. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) are used for characterization of the chemical composition and electronic structure of the samples. The roughness R_q of the Zn-Ni/TiO₂ is 49.5 nm, while for Zn-Co/TiO₂, the R_q value is 53.4 nm. The water contact angels are 93.2 and 95.5 for the Zn-Ni/TiO₂ and Zn-Co/TiO₂ systems, respectively. These investigations also show that the co-deposition of Zn and Ni forms a coating consisting entirely of Ni₂Zn₁₁, while the other alloy contains Zn, Co and the intermetallic compound CoZn₁₃. The corrosion resistance and protective ability are estimated by potentiodynamic polarization (PDP) curves, as well as polarization resistance (R_p) measurements for a prolonged test period (35 days). The results obtained are compared with the corrosion characteristics of ordinary zinc coating with an equal thickness. The experimental data presents the positive influence of the newly developed systems on the enhanced protective properties of low-carbon steel in a test environment causing a localized corrosion—lower corrosion current density of about one magnitude of order (~10⁻⁶ A.cm⁻² for both systems and ~10⁻⁵ A.cm⁻² for Zn) and an enhanced protective ability after 35 days (~10,000–17,000 ohms for the systems and ~900 ohms for Zn).

Nanotechnology has emerged as a promising option in combating the worsening situation with antibiotic resistance. We studied the antimicrobial effectiveness of four types of green synthesized zinc oxide nanoparticles (ZnO-NPs), obtained via Pluronic-assisted co-precipitation by lavender and thyme essential oils and their praseodymium-doped variants. Resazurin Microtiter Assay was applied to a panel of Gram-positive and Gram-negative bacteria from Risk 1 and 2 groups and the ESKAPE group. In relation to the pro-oxidative features of the ZnO-NPs, the production of superoxide dismutase (SOD) and catalase (CAT) in the tested microorganisms was also investigated, as these enzymes are important participants in the antioxidant defense of the bacterial cell and are considered virulence factors. We hypothesized that the sensitivity of microorganisms to the action of ZnO-NPs is related to their innate levels of antioxidant enzyme activity. The results showed that all types of studied ZnO-NPs had an antibacterial effect against the entire panel of tested strains, but with different potencies. The strongest effect was found for Arthrobacter nicotianae, Oerskovia paurometabola, Bacillus subtilis, and Escherichia coli. Less inhibition was observed for bacteria from Risk group 2 maybe due to their better antioxidant protection, especially for Pseudomonas aeruginosa. Praseodymium doping contributed to enhancing the bactericidal effect. A correlation between susceptibility of bacteria to ZnO-NPs and their antioxidant enzyme activity was observed.