Electron beam physical vapour deposition (EB-PVD) technology is a standard industrial method for the preparation of a thermal barrier coating (TBC) deposition on aeroengines. The internal stress of EB-PVD TBCs, including stress inside the top coating (TC) and thermal oxidation stress during long-term service is one of the key reasons for thermal barrier failures. However, research on the synergistic characterization of the internal stress of EB-PVD TBCs is still lacking. In this work, the stress inside the TC layer and the thermal oxidation stress of EB-PVD TBC during long-term thermal cycles were synergistically detected, combining Cr³⁺-PLPS and THz-TDS technologies. Based on a self-built THz-TDS system, stress-THz coefficients c₁ and c₂ of the EB-PVD TBC, which are the core parameters for stress characterization, were calibrated for the first time. According to experimental results, the evolution law of the internal stress of the TC layer was similar to that of the TGO stress, which were interrelated and influenced by each other. In addition, the internal stress of the TC layer was less than that of the TGO stress due to the columnar crystal microstructure of EB-PVD TBCs.

This paper investigates the streaming potentials’ behaviors when fluid flows through the micropores in bone. An experimental setup was developed for measuring the streaming potentials between two surfaces of a bone plate specimen. It was found that the streaming potentials measured increased almost linearly with time under a constant fluid pressure gradient, which does not agree with the prediction from the classical theory of streaming potentials. To explain the reasons associated with the results obtained, a theoretical model was proposed in which the electric charge densities on the inner surfaces of the capillary are unevenly distributed. A formula was developed for solving the model, and the solutions demonstrate that nonuniform accumulations of electric charges carried by the fluid on the inner surfaces of the microcanals in bone can induce streaming potentials which linearly increase with time during the driving air pressure holding period. This phenomenon represents the specific characteristics of bone. The solution implies that the streaming potentials in Haversian canals, lacunas and canaliculi are not affected by electro-viscous resistance in the bone fluid.

Alterations to the bone structure from cycle loadings can undermine its damage resistance at multiple scales. The accumulation of fatigue damage in a bone is commonly characterized by the reduction in the elastic modulus. In this study, nano-indentation was used for investigating microscopic damage evolution of bovine tibia samples subjected to fatigue loading. Indentation tests were conducted in the same 60 μm × 120 μm area with different degrees of damage, including fracture, and the evolution of reduced modulus was observed. The results showed that bone’s reduced modulus decreased significantly during the initial 40% of the life fraction, whereas it proceeded slowly during the remaining period. As the size of the residual indentations was about 4 μm in length, the degradation of bone’s reduced modulus reflected the accumulation of fatigue damage at smaller scales.

Micro Raman spectroscopy is an effective method to quantitatively analyse the internal stress of semiconductor materials and structures. However, the decoupling analysis of the stress components for {100} monocrystalline silicon (c-Si) remains difficult. In the work outlined, physical and simulation experiments were combined to study the influence of the objective lens numerical aperture (NA) on the Raman stress characterization. The physical experiments and simulation experiments show that the spectral results obtained by using lenses with different NAs can accurately obtain the principal stress sum but cannot decouple the components of the in-plane stress. Even if the spectral resolution of the simulated experiment is ideal (The random errors of the polarization directions of less than ±1° and the systematic random errors of less than ±0.02 cm⁻¹). The analysis based on the theoretical model demonstrates that the proportion of the principal stress sum in the Raman shift obtained in an actual experiment exceeded 98.7%, while the proportion of the principal stress difference part was almost negligible. This result made it difficult to identify the variable effects of different stress states from the experimental results. Further simulation experiments in this work verify that when the principal stress sum was identical, the differences in the Raman shifts caused by different stress states were much smaller than the resolution of the existing Raman microscope system, which was hardly possible to identify in the experimental results. It was proven that decoupling analysis of stress components using the large-NA objective lens lacked actual practicability.