ZnO is a semiconductor material that has important physical and chemical properties, which are frequently and significantly enhanced by the addition of impurities, such as doping. A study of the structural properties of pristine and functionalized (i.e., doped with Antimony and Tungsten) ZnO nanoparticles has been conducted for the photocatalyst-based degradation of methylene blue (MB) dye under both Ultraviolet (UV) and solar light. Authors have used a 1% concentration of dopant for doping purposes. The synthesized materials were characterized for structural analysis, functional group identification, spectroscopic measurements, and morphological examination using X-ray diffraction (XRD), Fourier transform-infrared (FTIR), UV-Vis spectroscopy (UV-Vis), and Field emission scanning electron microscope (FESEM) techniques. XRD analysis confirmed that the synthesized-doped materials retained the wurtzite hexagonal structure with a purity of 99%. Transmission electron microscope (TEM) analysis data reveals the average size of pure ZnO-NPs was found to be 7 nm; after doping the size was found to be increased to 18 nm and 9.55 nm, respectively, for ZnO-W and ZnO-Sb. As per FESEM analysis results, minor morphological changes were observed after doping. The Ultraviolet Differential reflectance spectroscopy UV-DRS study revealed the confirmation of ZnO doping with antimony and tungsten, which exhibited a blue shift. The decrease in the band-gap on doping makes the ZnO-NPs more efficient for photocatalytic applications. The photocatalytic efficiency of pristine and doped ZnO-NPs catalysts for methylene blue photocatalytic degradation (PCD) was analyzed under both UV and solar irradiation. This study analyzed the effect of pH, nano-photocatalyst dose, and initial dye concentration (ICD) on the PCD of MB. The obtained analytical results showed that the ideal conditions for the PCD of MB dye are as follows: pH = 9, the quantity of the nano-photocatalyst used was 300 mg/L, and an initial MB dye dose of 10 ppm. These conditions lead to a PCD of about 91% of the MB dye by using ZnO-Sb nano-photocatalyst on exposure to solar radiation. The reusability study also revealed the stability of nano-photocatalysts. The current research may pave the way for the removal of hazardous dyes from wastewater discharged by many industries.

Every year, a huge amount of water is polluted by various sources, out of which coal fly ash (CFA) is one of the major pollutants. CFA has a large number of toxic metals, which reaches water bodies by coming in contact with water or rain. Due to heavy-metal contamination, water becomes unfit for drinking for human beings, which in long term may cause several disorders. Thus, iron oxide nanoparticles (IONPs) recovered from waste, such as CFA, could be the most promising material for treating wastewater, due to their low-cost, recyclable nature and magnetic property. The synthesis of IONPs from CFA involves three sequential steps. The first step involves extraction of ferrous materials from CFA, followed by acidic treatment of ferrous materials to obtain acidic leachate, and lastly the precipitation of iron oxides by an alkali. The particle size of the synthesized IONPs varied from 30–70 nm and purity was about 90–93%, as confirmed by transmission electron microscope (TEM) and electron diffraction spectroscopy (EDS). Further, the synthesized IONPs were used for the remediation of various heavy metals, especially Pb and Cr ions from 20% CFA aqueous solutions. The heavy-metal removal efficiency of IONPs varied from 40–70%. The developed method suggests heavy-metal removal from wastewater by using an economical and greener route.

Every year a large amount of coal fly ash (CFA) is generated and dumped in fly ash ponds. Fly ash has numerous toxic heavy metals, which leads to water pollution due to the percolation of these heavy metals. Heavy metal toxicity has become a major issue for the whole globe. Moreover, CFA has several value-added minerals, such as silica, alumina, and ferrous in large amounts. Therefore, the synthesis of silica nanoparticles from CFA and their application for the removal of toxic heavy metals from fly ash aqueous solution will prove to be an economical and efficient approach. Here, in the present research work, investigators synthesized nanosilica from CFA by alkali dissolution and sol-gel methods and applied them for heavy metal removal. Firstly, CFA was treated with high molar NaOH, along with stirring and heating. Further, the sodium silicate leachate from CFA was treated with dilute HCl till the formation of a white gel at neutral pH. Purification of the nanosilica was achieved by treating with 1M HCl along with stirring followed by calcination at 400 °C for 4 h. The synthesized nanosilica was characterized by UV-Vis, Fourier transform infrared (FTIR), particle size analyzer (PSA), X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), electron diffraction spectroscopy (EDS), and high-resolution transmission electron microscope (HR-TEM). The sizes of the floral-shaped nanosilica particles were 20–70 nm, and the purity was 90–95%, as confirmed by microscopy and EDS, respectively. The XRD and FTIR revealed the amorphous nature of nanosilica. Finally, the potential of the nanosilica was assessed for the removal of heavy metals from 20% CFA aqueous solutions in batch experiments. The nanosilica showed about 40–90% removal of heavy metals (Al, Pb, Cd, Cu, Cr, Ni, Co, Zn, Mn) from the fly ash aqueous solution.