Self-compacting concrete (SCC) is a flowable concrete that can flow, fill and pass through congested area of reinforcement without segregation. As a material used in massive constructions, understanding of the effects of elevated temperature exposure on the properties of SCC is vital. The bond between concrete and embedded steel, which degrades with an increase in temperature, influences the load-carrying capacity and thus the fire resistance of reinforced concrete elements. The objective of this study was to evaluate the bond strength of SCC specimens made with fly ash, ground granulated blast-furnace slag (GGBFS) and expanded perlite aggregate (EPA) under elevated temperature exposure. EPA was introduced to enhance the fire endurance of the SCC. Slump flow, J-ring and V-funnel tests were conducted as per EFNARC guidelines to check the rheological characteristics of SCC. Specimens were exposed to elevated temperature following the ISO 834 standard fire curve. Pull-out tests were carried out to determine the bond strength of reference SCC specimens and specimens exposed to elevated temperature. Data from the tests showed that the SCC specimens made with a combination of GGBFS and EPA exhibited improved bond strength, both at room and elevated temperatures.

Self-Compacting Concrete (SCC) is a special concrete that can flow easily across congested reinforcements. Also, it is easy to work with and does not segregate. The present investigation aims at the design and development of sustainable SCC with the employment of industrial by-products such as Fly Ash (FA), Ground Granulated Blast Furnace Slag (GGBFS), and Expanded Perlite Aggregate (EPA). Four SCC mixes were developed to attain a target strength of 30 MPa. Workability tests (slump flow, J-ring, and V-funnel tests) were performed following the EFNARC guidelines to ensure fresh SCC properties. Detailed experiments were conducted to evaluate the durability characteristics of the developed SCC, such as water absorption, sorptivity, acid attacks (sulphuric, nitric, sulphate, and chloride), the Rapid Chloride Penetration Test (RCPT), and finally, the elevated temperature test. Weight loss, strength loss, and physical observations of the acid and temperature effects of SCC mixes were evaluated. Also, the study focuses on the cost and sustainable index of SCC mixes and compares them with OPC mixes. From the experimental data analysis, it was observed that the developed SCC showed excellent physical and mechanical properties with a considerable reduction in cement content. SCC specimens with FA and EPA exhibit excellent acid and temperature resistance. Following the sustainable analysis, it was noted that SCC mixes reduce about 15–17.2% of carbon emissions compared to the OPC mix.

Purpose: Building elements that are damaged by fire are often strengthened by fiber wrapping techniques. Self-compacting concrete (SCC) is an advanced building material that is widely used in construction due to its ability to flow and pass through congested reinforcement and fill the required areas easily without compaction. The aim of the research work is to examine the flexural behavior of SCC subjected to elevated temperature. This research work examines the effect of natural air cooling (AC) and water cooling (WC) on flexural behavior of M20, M30, M40 and M50 grade fire-affected retro-fitted SCC. The results of the investigation will enable the designers to choose the appropriate repair technique for improving the service life of structures. Design/methodology/approach: In this study, an attempt has been made to evaluate the flexural behavior of fire exposed reinforced SCC beams retrofitted with laminates of carbon fiber reinforced polymer (CFRP), basalt fiber reinforced polymer (BFRP) and glass fiber reinforced polymer (GFRP). Beam specimens were cast with M20, M30, M40 and M50 grades of SCC and heated to 925ºC using an electrical furnace for 60 min duration following ISO 834 standard fire curve. The heated SCC beams were cooled by either natural air or water spraying. Findings: The reduction in the ultimate load carrying capacity of heated beams was about 42% and 55% for M50 grade specimens that were cooled by air and water, respectively, in comparison with the reference specimens. The increase in the ultimate load was 54%, 38% and 27% for the specimens retrofitted with CFRP, BFRP and GFRP, respectively, compared with the fire-affected specimens cooled by natural air. Water-cooled specimens had shown higher level of damage than the air-cooled specimens. The specimens wrapped with carbon fiber could able to improve the flexural strength than basalt and glass fiber wrapping. Originality/value: SCC, being a high performance concrete, is essential to evaluate the performance under fire conditions. This research work provides the flexural behavior and physical characteristics of SCC subjected to elevated temperature as per ISO rate of heating. In addition attempt has been made to enhance the flexural strength of fire-exposed SCC with wrapping using different fibers. The experimental data will enable the engineers to choose the appropriate material for retrofitting.