The increase in the population creates an increased demand for construction activities with eco-friendly, sustainable, and high-performance materials. Insulated concrete form (ICF) is an emerging technology that satisfies the sustainability demands of the construction sector. ICF is a composite material (a combination of expanded polystyrene (EPS) and geopolymer concrete (GPC)) that enhances the performance of concrete (such as thermal insulation and mechanical properties). To investigate the axial strength performance, five different types of prototypes were created and tested. Type I (without reinforcement): (a) hollow EPS without concrete, (b) alternative cells of EPS filled with concrete, (c) and all the cells of EPS filled with concrete; and Type II (with reinforcement): (d) alternative cells of EPS filled with concrete; (e) and all the cells of EPS filled with concrete. Amongst all the five prototypes, two grades of GPC were employed. M15 and M20 grades are used to examine the effectiveness in terms of cost. For comparing the test results, a reference masonry unit was constructed with conventional clay bricks. The main aim of the investigation is to examine the physical and mechanical performance of sandwich-type ICFs. The presence of polystyrene in ICF changes the failure pattern from brittle to ductile. The result from the study reveals that the Type II prototype, i.e., the specimen with all the cells of EPS filled with concrete and reinforcement, possesses a maximum load-carrying capacity greater than the reference masonry unit. Therefore, the proposed ICF is recommended to replace the conventional load-bearing system and non-load-bearing walls.

The addition of nanomaterials to concrete efficiently fills the pores of the concrete, thereby improving its hardening characteristics. However, no research is available in the literature that investigated the influence of nano-cement (NC), nano-silica-fume (NS), nano-fly-ash (NF), and nano-metakaolin (NM), which are used as partial replacements for cement, on the impact strength (IS) of concrete at elevated temperatures. This issue is addressed herein. Nanomaterials were used in this study to replace 10%, 20%, and 30% of the cement in four different grades of concrete, starting from M20 to M50, at different temperatures. This nano-blended matrix was exposed to various temperatures ranging from 250 °C to 1000 °C, with an increment of 250 °C. In total, the results of 384 new tests were reported. In addition, morphological changes undergone by the concrete specimens were observed through a scanning electron microscope (SEM). The study revealed that the type of binder, proportion of binder, heating intensity, duration, and cooling type directly influenced the impact strength of concrete when subjected to elevated temperature. In comparison to NC, NF, NS, and NM, the mix with NC possessed superior performance when it was heated at 1000 °C. Prior to being subjected to elevated temperatures, the MK blended concrete mix performed well; however, when subjected to elevated temperatures, the MK blended concrete also experienced severe damage.