The CLP Publishing collects CLP journals and partnered optics and photonics journals, and provides readers an optical publishing platform with global influence. SPIE, OSA, CUP. Chinese Laser Press (CLP), established by Shanghai Institute of Optics and Fine Mechanics (SIOM), Chinese Academy of Sciences (CAS) and Chinese Optical Society (COS) in 2009, nowadays publishes eight journals and manages three online platforms.

CdS nanoneedles with different morphologies, structures, and growth modes have been grown on Ni-coated Si(100) surface under different experimental conditions by pulsed laser deposition method. The effects of catalyst layer, substrate temperature, and laser pulse energy on the growth of the CdS nanoneedles were studied in detail. It was confirmed that the formation of the molten catalyst spheres is the key to the nucleation of the CdS nanoneedles by observing the morphologies of the Ni catalyst thin films annealed at different substrate temperatures. Both the substrate temperature and laser pulse energy strongly affected the growth modes of the CdS nanoneedles. The secondary growth of the smaller nanoneedles on the top of the main nanoneedles was found at appropriate conditions. A group of more completed pictures of the growth modes of the CdS nanoneedles were presented.

Evenly separated crystalline CuIn_0.8Ga_0.2Se₂ (CIGS) nanoparticles are deposited on ITO-glass substrate by pulsed laser deposition. Such CIGS layers are introduced between conjugated polymer layers and ITO-glass substrates for enhancing light absorbance of polymer solar cells. The P3HT:PCBM absorbance between 300 and 650 nm is enhanced obviously due to the introduction of CIGS nanoparticles. The current density-voltage curves of a P3HT:PCBM/CIGS solar cell demonstrate that the short-circuit current density is improved from 0.77 to 1.20 mA/cm². The photoluminescence spectra show that the excitons in the polymer are obviously quenched, suggesting that the charge transfer between the P3HT:PCBM and CIGS occurred. The results reveal that the CIGS nanoparticles may exhibit the localized surface plasmon resonance effect just as metallic nanostructures. PACS 61.46. + w; 61.41.e; 81.15.Fg; 81.07.b

By the method of pulsed laser deposition of a Ni/C bilayer precursor films and annealing in air, amorphous carbon films were prepared on the surface of the capillary used for fabrication of optical fiber Fabry-Perot (FP) cavity pressure sensors. The surface morphologies of the coated and annealed carbon films were investigated through scanning electron microscopy. The images reveal that surface modification smoothes the irregular particles on the capillary surface and releases the stress induced by carbon and nickel deposition and oxy-hydrogen flame welding. Performance tests showed that the surface modified pressure sensors have good linearity for pressure response and the cavity length variations during the full cycle of pressure change is within 31 nm. Furthermore, thanks to the introduction of carbon films, the long-term stability of the cavity length can be kept within 10 nm during the tested 150 days.

Single-crystalline Cu7In3/CuIn0.8Ga0.2Se2 (CI/CIGS) core/shell nanowires are fabricated by pulsed laser deposition with Ni nanoparticles as catalyst. The CI/CIGS core/shell nanowires are made up of single-crystalline CI cores surrounded by single-crystalline CIGS shells. The CI/CIGS nanowires are grown at a considerably low temperature (350°C ~ 450°C) by vapor-liquid-solid mode combined with vapor-solid mode. The distribution density of the nanowires increases with the increasing of the deposition duration, and the substrate temperature determines the lengths of the nanowires. The U-V absorption spectra of the CIGS thin films with and without the CI/CIGS core/shell nanowires demonstrate that the CI/CIGS nanowires can remarkably enhance the absorption of CIGS thin films in the spectrum range of 300 to 900 nm.

By method of the pulsed laser deposition of Ni/C bilayer precursor films and annealing in N₂, ambient amorphous SiO₂ nanowires were prepared on fused quartz substrates. Field emission scanning electron microscopy images reveal that after annealing at the temperature of 1200°C for 1 h, the Ni/C films turn into dense nanowires with lengths and widths of several micrometers and tens of nanometers, respectively. Results of transmission electron microscopy, high resolution transmission electron microscopy, and energy dispersive X-ray spectroscopy fitted on it show that the nanowires are amorphous SiO₂ nanowires and that they are grown in the Ni-leading solid-liquid-solid mechanism. Besides, C particles can promote SiO₂ nanowires to grow longer in the forms of carbon and carbon monoxide.