In this research, corrugated Mg/Al clad sheet with good interface bonding was prepared with a rolling mill of upper corrugated roll and a lower flat roll under the conditions of 35% reduction and 400 °C. The mechanical properties of the corrugated Mg/Al clad sheet were studied using the transverse tensile test, Vickers microhardness and as well as its bending properties. Moreover, the interface bonding mechanism of the corrugated clad sheet was researched through three-dimensional contour analysis. The results showed that the UTS at the trough position was the highest (~296 MPa), and that the peak position was the lowest (~257 MPa). The maximum fracture EL at the peak position was ~13.4%, while the minimum fracture EL at the trough position was ~10.6%. In the transverse tensile process, the interface cracked first due to the uneven stress distribution in the matrixes. Then, the Mg sheet broke, and finally the Mg/Al clad sheet failed with final fracturing of the Al sheet. The microhardness of interface metal Al at the four positions was higher than that of the interface metal Mg, which was closely related to the dislocation strengthening of the Al sheet. The interface bonding mechanism of the corrugated Mg/Al clad sheet could be divided into four stages: extrusion deformation, rubbing fracture, compound extension and compound completion.

The utilization of 20CrNiMo/Incoloy 825 composite materials as high-pressure pipe manifold steel can not only improve the strength and hardness of the steel, but also improve its corrosion resistance. However, research on the heat treatment of 20CrNiMo/Incoloy 825 composite materials is still scarce. Thus, the aim of this study was to investigate the influence of solid solution treatment on the microstructure and properties of 20CrNiMo/Incoloy 825 composite materials. Firstly, the composite materials were subjected to solid solution treatment at temperatures ranging from 850 to 1100 °C with varied holding times of 1 h, 4 h, and 6 h. Microstructural analysis revealed that the solid solution treatment temperature had a more pronounced effect than the treatment time on the interface decarburization layer, carburization layer, and grain size. It was observed that the carburized layer thickness decreased while the decarburized layer thickness increased with an increase in the solid solution treatment temperature, oil cooling was found to enhance the hardness of the base layer of the composite materials, and the size of the original austenite grains of 20CrNiMo steel and Incoloy 825 increased with an increase in the solid solution treatment temperature. Secondly, the tensile properties, microhardness, and fracture morphology were evaluated after the composite materials underwent solid solution treatment at temperatures between 950 °C and 1100 °C for 1 h. The results indicated that increasing the solution temperature initially led to an increase in tensile strength and elongation after fracture, followed by a decrease; furthermore, the hardness of Incoloy 825 exhibited a declining trend, while the hardness of 20CrNiMo first decreased then increased. Thirdly, the shear properties and interfacial element diffusion of the composite materials were analyzed following solid solution treatment in a temperature range of 950 °C to 1100 °C for 1 h. The findings demonstrated that higher solid solution treatment temperatures induced full diffusion of Cr, Ni, and Fe atoms at the interface and softened the matrix, leading to an increase in the thickness of the diffusion layer and toughening of the composite interface. Therefore, the shear strength increased with an increase in the solid solution treatment temperature. Finally, the optimal solid solution treatment process for 20CrNiMo/Incoloy 825 composite materials was determined to be 1050 °C/1 h oil cooling, following which the composite materials had good comprehensive mechanical properties.

In this paper, an AZ31B Mg/Al clad plate with 5052 aluminum alloy as the cladding was successfully prepared by a new composite process of corrugated roll roughing + flat roll finishing. First, finite element simulation software was used to predict and analyze the rolling process. Subsequently, experimental research was carried out according to the simulation results, and clad plate samples under single corrugated rolling and corrugated–flat rolling processes were prepared. Finally, the differences between the two clad plates in shape quality, interface bonding state, and mechanical properties were systematically compared and analyzed. The results show that, compared with the traditional corrugated rolling process, the sheet formed by corrugated–flat rolling composite rolling has a flatter shape with no warpage, and its interface bonding quality is better. The specific performance is as follows: the mechanical properties were significantly improved, and the tensile strength and elongation reached 259.96 MPa and 8.11%, respectively, in the transverse direction (TD). This study provides a new strategy for the preparation of high-performance Mg/Al clad plates.