Polymers with a poly(ethylene glycol) backbone and mercaptomethyl side chains were synthesized by post-polymerization modification of hydroxymethyl side chains in three steps. As the starting point of the synthetic route, linear copolymers of ethylene oxide and glycidol with molar contents of glycidol repeating units of approximately 20, 40, 60, 80 and 100% were used. The polymer-bound hydroxyl groups were converted to thiol groups in three steps, comprising tosylation, introduction of a triphenylmethyl protected thiol and thiol deprotection by acid treatment. The degree of thiol-functionalization was controlled by the degree of functionalization of the starting material. The degree of conversion of hydroxyl groups to thiol groups determined by ¹H NMR spectroscopy was quantitative for copolymers with approximately 20 and 40% glycidol repeating units and 92, 81 and 87% for copolymers with approximately 60, 80 and 100% glycidol repeating units, respectively. Exemplarily, poly(glycidylthiol) obtained by conversion of poly(glycidol) was crosslinked with poly(ethylene glycol) diacrylate (PEG-DA) to yield hydrogels which supported adhesion and proliferation of human fibroblasts 48 h after cell seeding. Spatially defined and surface attached gel structures were fabricated by subsequent inkjet printing of poly(glycidylthiol) and PEG-DA solutions onto acrylated glass slides.

Structure and function of many transmembrane proteins are affected by their environment. In this respect, reconstitution of a membrane protein into a biomimetic polymer membrane can alter its function. To overcome this problem we used membranes formed by poly(1,4-isoprene-block-ethylene oxide) block copolymers blended with 1,2-diphytanoyl-sn-glycero-3-phosphocholine. By reconstituting the outer membrane protein OmpF from Escherichia coli into these membranes, we demonstrate functionality of this protein in biomimetic lipopolymer membranes, independent of the molecular weight of the block copolymers. At low voltages, the channel conductance of OmpF in 1 M KCl was around 2.3 nS. In line with these experiments, integration of OmpF was also revealed by impedance spectroscopy. Our results indicate that blending synthetic polymer membranes with phospholipids allows for the reconstitution of transmembrane proteins under preservation of protein function, independent of the membrane thickness.

In vivoself-endothelialization by endothelial cell adhesion on cardiovascular implants is highly desirable. DNA-oligonucleotides are an intriguing coating material with nonimmunogenic characteristics and the feasibility of easy and rapid chemical fabrication. The objective of this study was the creation of cell adhesive DNA-oligonucleotide coatings on vascular implant surfaces. DNA-oligonucleotides immobilized by adsorption on parylene (poly(monoaminomethyl-para-xylene)) coated polystyrene and ePTFE were resistant to high shear stress (9.5 N/m²) and human blood serum for up to 96 h. Adhesion of murine endothelial progenitor cells, HUVECs and endothelial cells from human adult saphenous veins as well as viability over a period of 14 days of HUVECs on oligonucleotide coated samples under dynamic culture conditions was significantly enhanced (P<0.05). Oligonucleotide-coated surfaces revealed low thrombogenicity and excellent hemocompatibility after incubation with human blood. These properties suggest the suitability of immobilization of DNA-oligonucleotides for biofunctionalization of blood vessel substitutes for improvedin vivoendothelialization.