Schematic of the galvanic corrosion evolution on η-phase (MgZn₂), β-phase (Al₃Mg₂), Q-phase (Al₄Cu₂Mg₈Si₇), and π-phase (Al₈Mg₃FeSi₆) coupled to aluminum at different pH values using the SVET current density map.

Polymer-based coatings are a long-established category of protective coatings for metals and alloys regarding corrosion inhibition. The polymer films can degrade, and when coated on metallic substrates, the degradation facilitates moisture and oxygen penetration, reducing the polymer film’s adhesion to the metallic substrate and exposing the substrate to extreme conditions capable of corrosion. For this reason, pigments, inhibitors, and other compatible blends are added to the polymer coating formulations to enhance adhesion and protection. To prevent the possible deterioration of inhibitor-spiked polymer coatings, inhibitors are encapsulated through diverse techniques to avoid leakage and to provide a controlled release in response to the corrosion trigger. This review discusses polymer-based coating performance in corrosion-causing environments to protect metals, focusing more on commercial steels, a readily available construction-relevant material used in extensive applications. It further beams a searchlight on advances made on polymer-based coatings that employ metal–organic frameworks (MOFs) as functional additives. MOFs possess a tailorable structure of metal ions and organic linkers and have a large loading capacity, which is crucial for corrosion inhibitor delivery. Results from reviewed works show that polymer-based coatings provide barrier protection against the ingress of corrosive species and offer the chance to add several functions to coatings, further enhancing their anti-corrosion properties.

The durability and functionality of many metallic structures are seriously threatened by corrosion, which makes the development of anticorrosive coatings imperative. This state-of-the-art survey explores the recent developments in the field of anticorrosive organic coatings modulated by innovations involving nano/microcontainers with porous matrices. The integration of these cutting-edge delivery systems seeks to improve the protective properties of coatings by enabling controlled release, extended durability, targeted application of corrosion inhibitors, and can be co-constructed to achieve defect filling by polymeric materials. The major highlight of this review is an in-depth analysis of the functionalities provided by porous nano/microcontainers in the active protection and self-healing of anticorrosive coatings, including their performance evaluation. In one case, after 20 days of immersion in 0.1 M NaCl, a scratched coating containing mesoporous silica nanoparticles loaded with an inhibitor benzotriazole and shelled with polydopamine (MSNs-BTA@PDA) exhibited coating restoration indicated by a sustained corrosion resistance rise over an extended period monitored by impedance values at 0.01 Hz frequency, rising from 8.3 × 10⁴ to 7.0 × 10⁵ Ω cm², a trend assigned to active protection by the release of inhibitors and self-healing capabilities. Additionally, some functions related to anti-fouling and heat preservation by nano/microcontainers are highlighted. Based on the literature survey, some desirable properties, current challenges, and prospects of anticorrosive coatings doped with nano/microcontainers have been summarized. The knowledge gained from this survey will shape future research directions and applications in a variety of industrial areas, in addition to advancing smart corrosion prevention technology.