Due to the excellent performance and low cost of the new aluminum-doped zinc oxide (AZO) film, it is expected to replace the mature indium-doped tin oxide (ITO) film. The research status and progress of AZO transparent conductive films are summarized in this review. Moreover, the structure, optoelectronic properties, and conductive mechanism of AZO thin films are also detailed. The thin films’ main preparation processes and the advantages and disadvantages of each process method are mainly discussed, and their application fields are expounded. AZO thin films with multicomponent composite structures are one of the promising development directions in transparent conductive oxide (TCO) thin films. The development of various preparation processes has promoted the production and application of thin films on a broad scale. Finally, some improvement schemes have been proposed to improve the comprehensive performance of the film. The industrialization prospects of the AZO film, as well as its great development potential in the digital world, are discussed.

Due to the severe harmful impacts of industrial dyeing wastewater on ecosystems and human health, proper treatment is crucial. Herein, the use of modified graphite as an adsorbent for dyeing wastewater treatment was investigated in this study. The graphite was oxidized and intercalated using a phosphoric acid–nitric acid–potassium permanganate system and then thermally treated at high temperatures to optimize its structure. By adjusting the thermal treatment temperature, the graphite adsorbent with varying porosity was obtained. The optimized graphite demonstrated significant improvement in adsorption performance for dyes and organic compounds, achieving a removal rate of over 85% for methylene blue (MB) dye. The optimal adsorption performance is achieved with a 1.6 mg modified graphite adsorbent at 60 °C under alkaline conditions for adsorbing 10 ppm MB. Adsorption kinetics and isotherm models were applied to elucidate the adsorption mechanisms. The results fit the Langmuir model, suggesting that monolayer homogeneous adsorption is favorable. Importantly, the results demonstrate that high-temperature treatment can significantly enhance the adsorption properties of coal-based graphite, supporting its application in dyeing wastewater treatment.

Brominated butyl rubber (BIIR) is a derivative of butyl rubber, with the advantage of high physical strength, good vibration damping performance, low permeability, aging resistance, weather resistance, etc. However, it is hard to avoid BIIR fiber sticking together due to serious swelling or merging, resulting in few studies on BIIR electrospinning. In this work, brominated butyl rubber membrane (mat) with BIIR microfiber has been prepared by electrospinning. The spinnability of elastomer BIIR has been explored. The factors influencing the morphology of BIIR microfiber membranes have been studied, including solvent, electrospinning parameters, concentration, and the rheological property of electrospinning solution. The optimal parameters for electrospinning BIIR have been obtained. A BIIR membrane with the ideal microfiber morphology has been obtained, which can be peeled from aluminum foil on a collector easily without being broken. Anti-bacterial property, the electrical conductivity of these membranes, and the mechanical properties of these samples were studied. The optimized BIIR electrospinning solution is Bingham fluid. The results of these experiments show that a BIIR membrane can be used in the field of medical prevention, wearable electronics, electronic skin, and in other fields that require antibacterial functional polymer materials.