Despite significant advancements in bio-based natural-fiber-reinforced composites, the recyclability/reprocessing of thermoset composites remains a persistent challenge that needs to be addressed. In the present study, an effort is made to provide a justification for the recyclability/reprocessing assessment of sandwich composite panels made with ‘recyclate’ (i.e., recycled flax/bio-based epoxy composite) cores and (flax/bio-based epoxy) skins produced by liquid composite molding. Resin transfer molding and vacuum-assisted resin infusion processes were used to investigate the influence of production processes on mechanical properties. Two different recyclate sizes—4 mm and 10 mm—were used to fabricate sandwich composite panels to study the effect of size on the mechanical properties of the panels. This study aims to compare the qualities of sandwich panels to those of virgin composite panels in terms of their physical (density) and mechanical properties (tensile and flexural). Additionally, the recyclate packing was verified by employing digital microscopy. The results illustrated that the sandwich panels made with the 4 mm recyclates exhibited better mechanical properties compared to those made with the 10 mm recyclates. In comparison with virgin composite panels, the sandwich composite panels made of flax fiber and (flax/epoxy) recyclate exhibited significantly higher flexural moduli, which was attributed to their moments of inertia. This article emphasizes recycling/reprocessing and demonstrates an effective closed-loop approach. Thus, by preserving the structural integrity of recyclates, sandwich panels could be advantageous for semi-structural applications.

Bio-based composites offer potential environmental benefits over fossil-based materials, but limited research exists on manufacturing processes with varying material combinations. This study performs a cradle-to-grave Life Cycle Assessment of five composite types to evaluate the role of fully and partially bio-based composites, focusing on the manufacturing stage. The composite materials include glass or flax fiber-based reinforcements embedded in polymer matrices based on a fossil epoxy, a partially bio-based epoxy, or epoxidized linseed oil, fabricated using vacuum-assisted resin infusion. Flax fibers in a partially bio-based epoxy achieve the lowest environmental impacts in most categories when assessed at equal geometry. Glass fiber composites exhibit a higher fiber volume content and material properties and thus demonstrate competitive environmental performance at equal absolute and normalized tensile strength. Composites using epoxidized linseed oil are the least advantageous, with the manufacturing stage contributing a majority of the environmental impacts due to their comparatively long curing times. These results are based on methodological choices and technical constraints which are discussed together with benchmarking against previous studies. While partially bio-based materials can provide a middle ground for enhancing composite environmental performance, the further optimization of bio-based material functionality regarding material properties and processability is pivotal to exploit the full potential of bio-based composites.

Increasing global concerns regarding environmental issues have driven significant advancements in the development of bio-based fiber reinforced polymer composites. Despite extensive research on bio-composites, there remains a noticeable gap in studies specifically addressing the challenges of repairing bio-composites for circular economy adoption. Traditional repair techniques for impacted composites, such as patching or scarf methods, are not only time-consuming but also require highly skilled personnel. This paper aims to highlight cost-effective repair strategies for the restoration of damaged composites, featuring flax fiber as the primary reinforcement material and distinct matrix systems, namely bio-based epoxy and bio-based vitrimer matrix. Glass fiber was used as a secondary material to validate the bio-based vitrimer matrix. The damage caused specifically by low impact is detrimental to the structural integrity of the composites. Therefore, the impact resistance of the two composite materials is evaluated using instrumented drop tower tests at various energy levels, while thermography observations are employed to assess damage evolution. Two distinct repair approaches were studied: the resin infiltration repair method, employing bio-based epoxy, and the reconsolidation (self-healing) repair method, utilizing the bio-based vitrimer matrix. The efficiency of these repair methods was assessed through active thermography and compression after impact tests. The repair outcomes demonstrate successful restoration and the maintenance of ultimate strength at an efficiency of 90% for the re-infiltration repair method and 92% for the reconsolidation repair method.

Bio-based composites offer potential environmental benefits over fossil-based materials, but limited research exists on manufacturing processes with varying material combinations. This study performs a cradle-to-grave Life Cycle Assessment of five composite types to evaluate the role of fully and partially bio-based composites, focusing on the manufacturing stage. The composite materials include glass or flax fiber-based reinforcements embedded in polymer matrices based on a fossil epoxy, a partially bio-based epoxy or epoxidized linseed oil, fabricated using vacuum-assisted resin infusion. Flax fibers in a partially bio-based epoxy achieve lowest environmental impacts in most categories when assessed at equal geometry. Glass fiber composites exhibit higher fiber volume content and material properties, and thus, demonstrate competitive environmental performance at equal absolute and normalized tensile strength. Composites using epoxidized linseed oil are least advantageous with the manufacturing stage contributing a majority of environmental impacts due to comparatively long curing times. These results are based on methodological choices and technical constraints, which are discussed together with benchmarking against previous studies. While partially bio-based materials can provide a middle-ground for enhancing composite environmental performance, further optimization of bio-based material functionality regarding material properties and processability is pivotal to exploit the full potential of bio-based composites.

This study examines the intrinsic optical enhancements of carbon fiber-reinforced polymers (CFRPs) achieved through the integration of magnesium oxide (MgO) nanoparticles, as well as Mg/MgO and titanium dioxide (TiO₂) thin films onto carbon fibers. Integration was performed by quasi-continuous electrophoretic deposition (EPD) and physical vapor deposition (PVD), respectively. Employing a customized electrophoretic cell, EPD facilitated uniform MgO nanoparticle deposition onto unsized carbon fibers, ensuring stable nanoparticle dispersion and precise fiber coating. As a result, the fibers exhibited increased ultraviolet (UV) reflectance, largely attributed to the optical properties of the protective MgO layer. In parallel, PVD enabled the deposition of Mg/MgO and TiO₂ thin films with tailored thicknesses, providing precise control over key optical parameters such as reflectivity and interference effects. Mg/MgO coatings demonstrated high UV reflectivity, while TiO₂ layers, with their varying refractive indices, generated vibrant colors in the visible (Vis) range through thickness-dependent light interference. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) assessed the quality, thickness, and uniformity of these thin films, and UV/Vis spectroscopy confirmed the influence of deposition parameters on the resulting optical performance. Post-lamination analyses revealed that both EPD and PVD modifications significantly enhanced UV reflectivity and allowed for customizable color effects. This dual strategy underscores the potential of combining EPD and PVD to develop advanced CFRPs with superior UV resistance, decorative optical features, and improved environmental stability.