To achieve future recycling targets and CO₂ and waste reduction, the transfer of plastic contained in mixed waste from thermal recovery to mechanical recycling is a promising option. This requires extensive knowledge of the necessary processing depth of mixed wastes to enrich plastics and their processability in polymer processing machines. Also, the selection of a suitable processing method and product application area requires appropriate material behaviour. This paper investigates these aspects for a commercial processed, mixed waste, and two different mixed polyolefin fractions. The wastes are processed at different depths (e.g., washed/not washed, sorted into polyethylene, polypropylene, polyethylene terephthalate, polystyrene/unsorted) and then either homogenised in the extruder in advance or processed heterogeneously in the compression moulding process into plates. The produced recyclates in plate form are then subjected to mechanical, thermal, and rheological characterisation. Most investigated materials could be processed with simple compression moulding. The results show that an upstream washing process improves the achievable material properties, but homogenisation does not necessarily lead to an improvement. It was also found that a higher treatment depth (recovery of plastic types) is not necessary. The investigations show that plastic waste recovery with simple treatment from mixed, contaminated wastes into at least downcycling products is possible.

Biobased plastics have the potential to be sustainable, but to explore their circularity further, current end-of-life options need to be broadened. Mechanical recycling is one of the most accepted methods to bring back plastics into the loop. Polyhydroxybutyrates (PHBs) are biobased and biodegradable in nature with promising properties and varied applications in the market. This study focuses on their potential for mechanical recycling by multiple extrusion cycles (E1–E5) and multi-faceted characterization of the virgin (V) and reprocessed materials from E1 to E5. The behavior is compared to polypropylene (PP) as a reference with a similar property profile, which has also been reprocessed five times. The thermal properties of both series showed a stable melting point and thermal decomposition temperature from thermal analyses (differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA)). However, a steady increase in the degree of crystallinity was observed which could counterbalance the decrease in molecular weight due to repeated extrusion measured by gel permeation chromatography and resulted in similar values of tensile strength across the cycles. The strain at break was impacted after the first extrusion, but no significant change was observed thereafter; the same was observed for impact strength. Even in scanning electron microscopy (SEM) images, virgin and E5 samples appeared similar, showing the stability of morphological characteristics. Fourier transform infrared spectroscopy (FTIR) results revealed that no new groups are being formed even on repeated processing. The deviation between the PHB and PP series was more predominant in the melt mass flow rate (MFR) and rheology studies. There was a drastic drop in the MFR values in PHB from virgin to E5, whereas not much difference was observed for PP throughout the cycles. This observation was corroborated by frequency sweeps conducted with the parallel plate method. The viscosity dropped from virgin to E1 and E2, but from E3 to E5 it presented similar values. This was in contrast to PP, where all the samples from virgin to E5 had the same values of viscosity. This paper highlights the possibilities of mechanical recycling of PHB and explains why future work with the addition of virgin material and other additives is an area to be explored.

Despite significant advancements in bio-based natural-fiber-reinforced composites, the recyclability/reprocessing of thermoset composites remains a persistent challenge that needs to be addressed. In the present study, an effort is made to provide a justification for the recyclability/reprocessing assessment of sandwich composite panels made with ‘recyclate’ (i.e., recycled flax/bio-based epoxy composite) cores and (flax/bio-based epoxy) skins produced by liquid composite molding. Resin transfer molding and vacuum-assisted resin infusion processes were used to investigate the influence of production processes on mechanical properties. Two different recyclate sizes—4 mm and 10 mm—were used to fabricate sandwich composite panels to study the effect of size on the mechanical properties of the panels. This study aims to compare the qualities of sandwich panels to those of virgin composite panels in terms of their physical (density) and mechanical properties (tensile and flexural). Additionally, the recyclate packing was verified by employing digital microscopy. The results illustrated that the sandwich panels made with the 4 mm recyclates exhibited better mechanical properties compared to those made with the 10 mm recyclates. In comparison with virgin composite panels, the sandwich composite panels made of flax fiber and (flax/epoxy) recyclate exhibited significantly higher flexural moduli, which was attributed to their moments of inertia. This article emphasizes recycling/reprocessing and demonstrates an effective closed-loop approach. Thus, by preserving the structural integrity of recyclates, sandwich panels could be advantageous for semi-structural applications.