The prevalence of complications due to the presence of biofilms in dental implant surfaces and their relationship with peri-implant diseases, namely peri-implantitis, remain difficult problems to overcome. The information available about the application of electric current on dental implant biofilms; its parameters, namely current level, voltage and exposure time; and related effects are still not enough to understand which individual mechanisms are caused by this technique, culminating in the decrease or eradication of the biofilm. The purpose of this narrative review, based on a systematic search, is to understand the effect of electric current directly applied to biofilms present in dental implants and which parameters are used. For the systematic search, electronic databases including MEDLINE/PubMed, Scopus, and Web of Science, up to and including November 2023, were searched. Seven studies were included. A 12-item checklist was used to assess their methodological quality. All studies used direct/constant electric current; however, that use was not achieved by the same protocol/set-up. Parameters such as current, voltage, resistance, and actuation time were different in all studies. Monospecies and multi-species biofilm were used in the substrate made of titanium. The results indicate that the use of constant and alternating electric current directly applied to dental implant’s surfaces is a promising way to treat problems related to biofilms and peri-implant diseases. Future trials, namely in vivo tests, are necessary to reveal all the potential of this treatment.

Dental decay still presents a major health problem among children. Its treatment usually requires the use of stainless steel crowns. This study compares the wear behavior of 316 L stainless steel and polyetheretherketone (PEEK) composite under identical test conditions. The wear tests were conducted in a reciprocating ball-on-plate tribometer (Plint TE67/R) using alumina balls as a counterface and artificial saliva as a lubricant at 37 °C to faithfully mimic oral conditions. The coefficient of friction (COF) and specific wear rate (k) values were determined and SEM/EDS examinations were performed to identify the predominant wear mechanisms. Results showed that PEEK exhibited a significantly lower coefficient of friction (COF = 0.094 ± 0.004) and thus lower wear volume (ΔV = 0.0078 ± 0.0125 mm³) and higher wear resistance, with an average value of specific wear rate of k = 9.07 × 10⁻⁶ mm³N⁻¹m⁻¹ when compared to stainless steel (COF = 0.32 ± 0.03, ΔV = 0.0125 ± 0.0029 mm³, k = 1.45 × 10⁻⁵ mm³N⁻¹m⁻¹). PEEK was revealed to be a potential material for use in pediatric crowns due to its high wear resistance while overcoming the disadvantages associated with steel at both an aesthetic and biological level.

Tooth loss during the lifetime of an individual is common. A strategy to treat partial or complete edentulous patients is the placement of dental implants. However, dental implants are subject to bacterial colonization and biofilm formation, which cause an infection named peri-implantitis. The existing long-term treatments for peri-implantitis are generally inefficient. Thus, an electrical circuit was produced with zirconia (Zr) samples using a hot-pressing technique to impregnate silver (Ag) through channels and holes to create a path by LASER texturing. The obtained specimens were characterized according to vitro cytotoxicity, to ensure ZrAg non-toxicity. Furthermore, samples were inoculated with Staphylococcus aureus using 6.5 mA of alternating current (AC). The current was delivered using a potentiostat and the influence on the bacterial concentration was assessed. Using AC, the specimens displayed no bacterial adhesion (Log 7 reduction). The in vitro results presented in this study suggest that this kind of treatment can be an alternative and promising strategy to treat and overcome bacterial adhesion around dental implants that can evolve to biofilm.

Dental materials are well-established, with stainless steel 316L (SS) still being a common choice for components such as pediatric crowns and abutments. However, SS has some drawbacks, particularly in terms of mechanical properties and, more importantly, aesthetics, due to its metallic gray color. In this sense, PEEK (polyetheretherketone) has emerged as a promising material for dental applications, combining good mechanical properties with improved aesthetic features. This study compared the cytocompatibility of PEEK TiO₂ composite and SS using human fetal osteoblasts (hFOB) and human gingival fibroblasts (HGF). Cytocompatibility was evaluated over 1–7 days through metabolic activity and alkaline phosphatase (ALP) assays. Additionally, bacterial adhesion was assessed using Staphylococcus aureus and Pseudomonas aeruginosa in both monoculture and co-culture. The results showed that both materials were non-cytotoxic and supported cell growth. Notably, after 7 days of culture, PEEK TiO₂ surfaces promoted approximately 7% higher ALP activity than stainless steel, demonstrating a significantly enhanced osteogenic response (p < 0.01). Moreover, at day 7, PEEK TiO₂ promoted ~25% higher metabolic activity in HGF cells compared to SS. Regarding the bacterial adhesion, it was consistently low in PEEK TiO₂ for both S. aureus and P. aeruginosa, with a marked reduction (~50%) observed for P. aeruginosa under co-culture conditions. PEEK TiO₂ demonstrated enhanced biological performance and lower bacterial adhesion compared with SS, highlighting its potential as a biocompatible and aesthetically promising option for dental applications, including pediatric crowns.