The aim of the work is to compare the properties of nanohydroxyapatite coatings obtained using the electrophoretic deposition method (EDP) at 10 V, 20 V, and 30 V, and with deposit times of 2 and 5 min. The primary sedimentation was used to minimize the risk of the formation of particle agglomerates on the sample surface. Evaluation of the coating was performed by using a Scanning Electron Microscope (SEM), Energy-Dispersive Spectroscopy (EDS), Atomic Force Microscopy (AFM), optical profilometer, drop shape analyzer, and a nanoscratch tester. All of the coatings are homogeneous without any agglomerates. When low voltage (10 V) was used, the coatings were uniform and continuous regardless of the deposition time. The increase in voltage resulted in the formation of cracks in the coatings. The wettability test shows the hydrophilic behavior of the coatings and the mean contact angle values are in the range of 20–37$°$. The coatings showed excellent adhesion to the substrate. The application of a maximum force of 400 mN did not cause delamination in most coatings. It is concluded that the optimal coating for orthopedic implants (such as hip joint implants, knee joint implants or facial elements) is obtained at 10 V and 5 min because of its homogeneity, and a contact angle that promotes osseointegration and great adhesion to the substrate.

The increasing demand for titanium and its alloys used for implants results in the need for innovative surface treatments that may both increase corrosion resistance and biocompatibility and demonstrate antibacterial protection at no cytotoxicity. The purpose of this research was to characterize the effect of two-stage anodization—performed for 30 min in phosphoric acid—in the presence of hydrofluoric acid in the second stage. Scanning electron microscopy, atomic force microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, Raman spectroscopy, glow discharge optical emission spectroscopy, nanoindentation and nano-scratch tests, potentiodynamic corrosion studies, and water contact angle measurements were performed to characterize microstructure, mechanical, chemical and physical properties. The biologic examinations were carried out to determine the cytotoxicity and antibacterial effects of oxide coatings. The research results demonstrate that two-stage oxidation affects several features and, in particular, improves mechanical and chemical behavior. The processes influencing the formation and properties of the oxide coating are discussed.

The 9Ni martensitic steels have a martensitic microstructure which contains retained austenite after solution heat treatment and water quenching. Under low cycle fatigue, extrusions formed at the surface of the material and were very close to martensite lath boundaries. The presence of retained austenite at martensite laths has been highly suspected to impact the cyclic plasticity. However, the nano-size of the austenitic phase makes it difficult to obtain clear evidence of its role. The paper focuses on the precise determination of these extrusions and the link with the retained austenite. The paper also emphasizes the innovative and promising use of magnetic force microscopy (MFM) to document cyclic plasticity of a 9Ni steel. It is shown that electron microscopies, even the most advanced ones, may be unsuccessful in reaching this goal, while magnetic force microscopy (MFM) overcame the difficulty. This technique has allowed imaging of both the extrusion and the retained austenite. These analyses confirm that the fatigue extrusions originated from a local displacement of martensite lath. The proposed mechanism, in which the retained austenitic film acts as a lubricant film or greasy film promoting a flowing of martensite along the interfaces, is unambiguously demonstrated.