This article reviews biochar production and its potential applications across various sectors, including agriculture, environmental remediation, and energy storage. It emphasizes the critical role of feedstock source and process parameters, such as residence time, heating rate, and temperature, in determining biochar’s properties. Although extensive research has been conducted on the physical and chemical properties of biochar, there remains a significant gap in evaluating its practical applications. This paper emphasizes the role of Multi-Criteria Decision Analysis (MCDA) as a valuable tool for optimizing both biochar production and its application strategies. By exploring scholarly articles and patents, it offers insights into biochar production techniques, characterization methods, and the importance of process optimization for sustainable and efficient biochar use in real-world scenarios.

This work concerns the preparation of Pt/AC catalysts (Pt supported on activated carbon) and their application to the synthesis of hydrocarbon biofuels through the HEFA (hydroprocessing of esters and fatty acids) route. The key motivation for the work was that catalysts based on sulfided Mo supported on γ-Al₂O₃, traditionally employed in the hydroprocessing of petroleum derivatives, (i) are unstable in the HDO (hydrodeoxygenation) of biomass-derived feedstocks and (ii) can contaminate the resulting biofuels with sulfur. In this context, a systematic study on the effects of preparation conditions on the properties of the resulting Pt/AC catalysts and their performance in HEFA was carried out for the first time. Efficient catalysts were obtained, which led to the complete deoxygenation of lauric acid and coconut oil, yielding products composed primarily of n-alkanes. The highest HDO activity was verified for the catalyst prepared using as a support an AC previously subjected to thermal treatment up to 800 °C in a H₂ atmosphere (which removed most of the surface acidic oxygenated groups), depositing Pt over the surface of this support via wet impregnation using a H₂PtCl₆ solution acidified with HCl. The obtained results showed the great potential of the Pt/AC catalysts for the production of hydrocarbon biofuels through the HEFA route.

N-containing carbon-based materials have been employed with claimed improved performance as an adsorbent of acidic molecules, volatile organic compounds (VOC), and metallic ions; catalyst; electrocatalyst; and supercapacitor. In this context, the present work provides valuable insights into the preparation of N-doped activated carbons (ACs) by thermal treatment in NH₃ atmosphere (ammonization). A commercial AC was submitted to two kinds of pretreatment: (i) reflux with dilute HNO₃; (ii) thermal treatment up to 800 °C in inert atmosphere. The original and modified ACs were subjected to ammonization up to different temperatures. ACs with N content up to ~8% were achieved. Nevertheless, the amount and type of inserted nitrogen depended on ammonization temperature and surface composition of the starting material. Remarkably, oxygenated acidic groups on the surface of the starting material favored nitrogen insertion at low temperatures, with formation of mostly aliphatic (amines, imides, and lactams), pyridinic, and pyrrolic nitrogens. In turn, high temperatures provoked the decomposition of labile aliphatic functions. Therefore, the AC prepared from the sample pre-treated with HNO₃, which had the highest content of oxygenated acidic groups among the materials submitted to ammonization, presented the highest N content after ammonization up to 400 °C but the lowest content after ammonization up to 800 °C.

The modification of fatty substrates using heterogeneous catalysts have extensive industrial application and has an emphatic position in a sustainable context. Herein ruthenium, nickel, cobalt and copper-doped ruthenium, supported on hypercrosslinked polystyrene (HPS) catalysts were prepared by wet impregnation, characterized and applied on the modification of canola fatty acid methyl esters (FAME). The characterization showed a dispersive effect of doping metals over the ruthenium particles, the presence of acid sites and overall surface morphology, which allows targeting potential applications. The chosen modifications consisted of hydrogenation, hydroformylation, oxidative cleavage and deoxygenation, resulting in superb catalytic activities of over 99% conversions for hydrogenation and deoxygenation. The simplicity of the canola FAME composition allows the understanding of the catalytic processes and allows the upscale of more complex FAME matrixes. Finally, the obtained data stimulates further optimization studies for each application with a variation on the catalysts and the usage of residual fatty substrates, greatly enhancing the sustainability profile of the systems.

N-containing carbon-based materials have been employed with claimed improved performance as adsorbent of acidic molecules, VOC and metallic ions, catalyst, electrocatalyst and supercapacitor. In this context, the present work provides valuable insights into the preparation of N-doped activated carbons (ACs) by thermal treatment in NH3 atmosphere (ammonization). A commercial AC was submitted to two kinds of pre-treatment: (i) reflux with dilute HNO3; (ii) thermal treatment up to 800 oC in inert atmosphere. The original and modified ACs were subjected to ammonization up to different temperatures. ACs with N content up to 8% were achieved. Nevertheless, the amount and type of inserted nitrogen depended on ammonization temperature and surface composition of the starting material. Remarkably, oxygenated acidic groups on the surface of the starting material favored nitrogen insertion at low temperatures, with formation of mostly aliphatic (amines, imides, and lactams), pyridinic and pyrrolic nitrogens. In turn, high temperatures provoked the decomposition of labile aliphatic functions. Therefore, the AC prepared from the sample pre-treated with HNO3, which had the highest content of oxygenated acidic groups among the materials submitted to ammonization, presented the highest N content after ammonization up to 400 oC, but the lowest content after ammonization up to 800 oC.