The antibacterial activity, and the effect of the application of additional topical fluoride on the bacterial activity, biofilm formation, and surface roughness of new-generation hybrid/fluoride-releasing materials were investigated. Two hundred and forty specimens were prepared in split Teflon molds (8 × 2 mm) from a resin composite (as negative control: G-aenial A’Chord/GC), Equia Forte HT Fil(GC), Equia Forte HT Fil+Equia Forte Coat, Riva Self-Cure (SDI), Riva Self-Cure+Equia Forte Coat, Zirconomer (Shofu), Beautifil II (Shofu), and Riva Silver (Shofu). Penicillin G,1U was used as positive control. The antibacterial activity was evaluated by the agar diffusion test immediately after the materials set using Streptococcus mutans (S. mutans) and Lactobacillus casei (L. casei), and repeated after application of 0.20% w/w (900 ppm) topical fluoride. The biofilm formation of S. mutans on each material was quantified by crystal violet staining. Surface roughness of the specimens was measured by a profilometer. The data were analyzed by Kruskal–Wallis, Dunn’s, one-way ANOVA, and Tukey’s HSD tests (p < 0.05). None of the tested restorative materials showed antibacterial activity and no inhibition zones were observed after treatment of the restoratives with additional topical fluoride. There were significant differences among the groups in terms of biofilm formation (p < 0.005). Equia Forte HT Fil with and without coating showed the lowest, while Riva self-cure without coating and Zirconomer showed the highest biofilm accumulation. None of the new-generation hybrid/fluoride-releasing materials demonstrated antibacterial activity and additional topical fluoride application did not make any change. Biofilm formation of the tested materials differed. All tested materials showed different surface roughness values (p < 0.005). Characteristics and compositions of the materials seemed to be more effective than the surface roughness.

Resistance to antibiotics is recognized as one of the biggest threats to human health worldwide. Frequent and unnecessary use of antibiotics has caused infectious agents to adapt to antibiotics and thus drugs have become less effective. The resistance to many antibiotics necessitates the discovery of new antibiotics. In this study, two new and 23 previously reported 2-pyrazoline derivatives and one hydrazone derivative were evaluated for their in vitro antibacterial and antifungal activities. For the determination of the minimum inhibitory concentration (MIC) values of compounds, microbroth dilution was used. The antimicrobial activities of the compounds were found in a wide range with MIC values of 32-512 μg/mL. The synthesized compounds showed moderate antimicrobial activity compared with the standards. They can be used as lead molecules for the synthesis of more effective compounds.

This study investigates the effects of the antiperspirant aluminum chlorohydrate on the development of antibiotic resistance in commensal Staphylococcus epidermidis isolates. The isolates were exposed to aluminum chlorohydrate for 30 days. The bacteria that developed resistance to oxacillin and ciprofloxacin were isolated, and the expression levels of some antibiotic resistance genes were determined using quantitative reverse transcriptase PCR. Before and after exposure, the minimum inhibitory concentration (MIC) values of the bacteria were determined using the microdilution method. A time-dependent increase was observed in the number of bacteria that developed resistance and increased MIC values. Consistent with the ciprofloxacin resistance observed after exposure, an increase in norA, norB/C, gyrA, gyrB, parC, and parE gene expression was observed. In addition to aluminum chlorohydrate exposure, oxacillin resistance was observed in all test bacteria in the group only subcultured in the medium, suggesting that phenotypic resistance cannot be correlated with chemical exposure in light of these data. The increase in mecA gene expression in selected test bacteria that acquired resistance to oxacillin after exposure compared with control groups suggests that the observed resistance may have been related to aluminum chlorohydrate exposure. To our knowledge, this is the first time in the literature that the effects of aluminum chlorohydrate as an antiperspirant on the development of antibiotic resistance in Staphylococcus epidermidis have been reported.