The antibacterial activity, and the effect of the application of additional topical fluoride on the bacterial activity, biofilm formation, and surface roughness of new-generation hybrid/fluoride-releasing materials were investigated. Two hundred and forty specimens were prepared in split Teflon molds (8 × 2 mm) from a resin composite (as negative control: G-aenial A’Chord/GC), Equia Forte HT Fil(GC), Equia Forte HT Fil+Equia Forte Coat, Riva Self-Cure (SDI), Riva Self-Cure+Equia Forte Coat, Zirconomer (Shofu), Beautifil II (Shofu), and Riva Silver (Shofu). Penicillin G,1U was used as positive control. The antibacterial activity was evaluated by the agar diffusion test immediately after the materials set using Streptococcus mutans (S. mutans) and Lactobacillus casei (L. casei), and repeated after application of 0.20% w/w (900 ppm) topical fluoride. The biofilm formation of S. mutans on each material was quantified by crystal violet staining. Surface roughness of the specimens was measured by a profilometer. The data were analyzed by Kruskal–Wallis, Dunn’s, one-way ANOVA, and Tukey’s HSD tests (p < 0.05). None of the tested restorative materials showed antibacterial activity and no inhibition zones were observed after treatment of the restoratives with additional topical fluoride. There were significant differences among the groups in terms of biofilm formation (p < 0.005). Equia Forte HT Fil with and without coating showed the lowest, while Riva self-cure without coating and Zirconomer showed the highest biofilm accumulation. None of the new-generation hybrid/fluoride-releasing materials demonstrated antibacterial activity and additional topical fluoride application did not make any change. Biofilm formation of the tested materials differed. All tested materials showed different surface roughness values (p < 0.005). Characteristics and compositions of the materials seemed to be more effective than the surface roughness.

Background: The aim of this study was to evaluate the effects of incorporation of hydroxyapatite (HA) derived from cuttlefish bone on the microhardness, surface roughness (SR), and fluoride release (FR) of conventional cure, and resin-modified glass-ionomer cement. Methods: There were four groups for each tested material; experimental glass-ionomer were made by addition and of 2, 5, and 10 wt % HA respectively to conventional glass-ionomers Fuji II LC and Fuji IX GP Extra. One group was prepared without the addition of HA particles. For SR and microhardness measurements sectional Teflon molds (5 mm in diameter and 2 mm deep) were used to prepare 10 samples per group (n = 80). The samples were stored in distilled water at 37 °C for 7 days prior to testing. The SR was measured using a contact type profilometer and the microhardness was determined using a Vickers micro-hardness tester at a load of 980 g for 15 s. For FR measurements, there were six samples per group (n = 48), prepared in Teflon molds (8 mm in diameter and 2 mm deep). The FR was measured with an ionoselective electrode in triplicates after 24 h, 7 days, and 45 days. Statistical analysis was performed using one-way ANOVA with Tukey post-hoc test. Results and Conclusion: Microhardness values obtained for Fuji II modified with 10 wt % HA were significantly higher compared to the other two groups tested. Comparison of materials with respect to SR showed significant difference between them (p < 0.0001) with Fuji II and Fuji IX modified with HA having higher SR values. Regarding FR, Fuji IX showed statistically significant higher results than Fuji II, independently of HA modification, and groups modified with 2 and 5 wt % HA showed significantly increased fluoride release in all three time points.

The surface gloss, radiopacity and enamel/dentin shear bond strengths (SBS)s of five commercially available contemporary universal composite resins (CR)s were examined. The tested universal CRs were as follows: G-aenial A’CHORD (GA), Charisma Diamond (CD), Neo Spectra^TMST(NS), Filtek(F) and Estelite Asteria(EA). Twelve cylindrical specimens per group were fabricated and gloss measurements were performed using a gloss meter after polishing and darkening. Five specimens of each group were radiographed using a CMOS sensor alongside an aluminum stepwedge, human enamel and dentin. The mean gray values were measured with a computer program. A total of 120 bonded human enamel and dentin specimens were subjected to SBS test. To analyze surface gloss, radiopacity and SBS we used Kruskall–Wallis, Wilcoxon signed rank, Welch tests and one-way ANOVA. Games–Howell, Tukey’s HSD tests, and Dunn’s multiple comparisons were used for multiple comparisons (p < 0.05). In terms of gloss units of the materials after polishing and darkening, the highest surface gloss was achieved with GA, followed by NS, F, CD and EA (p < 0.001). All the tested CRs showed significantly higher radiopacity values in comparison with dentin (p < 0.05). CD and NS presented higher radiopacity values, while other CRs were, in decreasing order; F, GA and EA (p < 0.001). The SBS ranking varied for enamel and dentin, and the adhesive failure was detected at a higher rate. Commercially available contemporary universal CRs display different surface gloss, radiopacity and SBS properties.