This work aimed to compare the effect of four new toothpastes (P1–P4) based on pure and biomimetic substituted nano-hydroxyapatites (HAPs) on remineralization of human enamel. Artificially demineralized enamel slices were daily treated for ten days with different toothpastes according to the experimental design. Tooth enamel surfaces were investigated using atomic force microscope (AFM) images and surface roughness (Ra) determined before and after treatment. The surface roughness of enamel slices was statistically analyzed by one-way ANOVA and Bonferroni’s multiple comparison test. X-ray diffraction (XRD) and Fourier transform infrared (FTIR) data revealed the HAP structure with crystal sizes between 28 and 33 nm and crystallinity between 29 and 37%. The average size of HAP particles was found to be between 30 and 40 nm. The Ra values indicated that P3 (HAP-Mg-Zn-Sr-Si) toothpaste was the most effective after 10 days of treatment, leading to the lowest mean roughness. The P3 and P2 (HAP) toothpastes were found to be effective in promoting remineralization. Specifically, their effectiveness can be ranked as follows: P3 = P2 > P4 (HAP-Mg-Zn-Si) > P1 (HAP-Zn), considering both the chemical composition and the size of their constitutive nanoparticles. The proposed toothpastes might be used successfully to treat early tooth decay.

To address tooth enamel demineralization resulting from factors such as acid erosion, abrasion, and chronic illness treatments, it is important to develop effective daily dental care products promoting enamel preservation and surface remineralization. This study focused on formulating four toothpastes, each containing calcined synthetic hydroxyapatite (HAP) in distinct compositions, each at 4%, along with 1.3% birch extract. Substitution elements were introduced within the HAP structure to enhance enamel remineralization. The efficacy of each toothpaste formulation was evaluated for repairing enamel and for establishing the dynamic of the remineralization. This was performed by using an in vitro assessment of artificially demineralized enamel slices. The structural HAP features explored by XRD and enamel surface quality by AFM revealed notable restorative properties of these toothpastes. Topographic images and the self-assembly of HAP nanoparticles into thin films on enamel surfaces showcased the formulations’ effectiveness. Surface roughness was evaluated through statistical analysis using one-way ANOVA followed by post-test Bonferroni’s multiple comparison test with a p value < 0.05 significance setting. Remarkably, enamel nanostructure normalization was observed within a short 10-day period of toothpaste treatment. Optimal remineralization for all toothpastes was reached after about 30 days of treatment. These toothpastes containing birch extract also have a dual function of mineralizing enamel while simultaneously promoting enamel health and restoration.

This research work aims to develop functional toothpastes with combined enamel remineralization and antibacterial effects using nano-hydroxyapatites (nHAPs) and birch extract. Eleven toothpastes (notated as P1–P11) were designed featuring different concentrations of birch extract and a constant concentration of pure nHAPs or substituted nHAPs (HAP-5%Zn, HAP-0.23%Mg-3.9%Zn-2%Si-10%Sr, and HAP-2.5%Mg-2.9%Si-1.34%Zn). In vitro assessments involved treating artificially demineralized enamel slices and analyzing surface repair and remineralization using Atomic Force Microscopy (AFM). The Agar Disk Diffusion method was used to measure antibacterial activity against Enterococcus faecalis, Escherichia coli, Porphyromonas gingivalis, Streptococcus mutans, and Staphylococcus aureus. Topographic images of enamel structure and surface roughness, as well as the ability of nHAP nanoparticles to form self-assembled layers, revealed excellent restorative properties of the tested toothpastes, with enamel nanostructure normalization occurring as soon as 10 days after treatment. The outcomes highlighted enamel morphology improvements due to the toothpaste treatment also having various efficacious antibacterial effects. Promising results were obtained using P5 toothpaste, containing HAP-5%Zn (3.4%) and birch extract (1.3%), indicating notable remineralization and good antibacterial properties. This study represents a significant advancement in oral care by introducing toothpaste formulations that simultaneously promote enamel health through effective remineralization and bacterial inhibition.

A nanocomposite made from hydroxyapatite (HAP) and silver nanoparticles (AgNPs), namely HAP-4.5 wt% AgNPs, is reported. HAP was prepared using a wet precipitation technique, and AgNPs were made by reducing silver nitrate with glucose in basic medium. HAP, AgNPs and HAP-4.5 wt% AgNPs composite were characterized by X-ray diffraction (XRD), SEM - energy dispersive X-ray spectroscopy (EDS) and different imagistic methods: TEM and AFM. The antibacterial effect of the HAP-4.5 wt% AgNPs nanocomposite was tested using diffusion technique in nutritive agar on two pathogenic species, one Gram-negative (Salmonella typhimurium) and one Gram-positive (Bacillus cereus) and promising results were obtained. This hydroxyapatite-silver nanocomposite can be employed as a potential antimicrobial coating for dental and orthopedic implants, or they can be utilized such as bone cements in clinical procedures.

The use of toothpastes is the best way to combat enamel loss and degradation. When they also contain hydroxyapatite nanoparticles, HAP NPs, the tooth enamel can be restored by remineralization. In this study, we developed two types of toothpastes, one with nano sized HAP, noted P1, and the other with nano multi-substituted hydroxyapatite (ms-HAP, HAP-Mg-Zn-Si), noted P2, which were used to treat the artificially demineralized teeth enamel surface. The remineralization efficacy of the two toothpastes was determined on artificially created enamel lesions by suspending healthy enamel slices in demineralizing solution, made of orthophosphoric acid of 37.5% for 90 s. For this purpose, six extracted third molars were collected and twenty-four enamel slices were cut and arbitrarily allocated to the four groups, namely n = 6 enamel slices for each group. One group served as untreated (natural) enamel control, and another group comprised demineralized enamel and two test groups, firstly demineralized, and then, they were treated with toothpastes P1 and P2, respectively, each of them for ten days, and finally were noted P1 and P2 enamel surfaces. The surface morphology and roughness of all enamel specimens were studied by atomic force microscopy (AFM) before and after applying the treatment with the toothpastes. The toothpastes effect was evidenced by the average diameter of ceramic nanoparticles deposited within the superficial smooth layer on enamel surface having, at the completion of 10 days treatment, a low surface roughness close to that of natural enamel. This in vitro comparative study demonstrated that both toothpastes P1 and P2 can promote surface enamel repair by remineralization and the formation of a protective hydroxyapatite coating layer on the enamel surface treated with these toothpastes.

Due to the ions in its structure, that have a variety of important roles in bone metabolism, forsterite (FS, Mg2SiO4) is a promising candidate for orthopedic and dental applications. This paper studies forsterite synthesized through two methods, namely sol-gel (FSsg) and precipitation (FSpp), based on a thermodynamic approach. Therefore, the precursor gel and precipitate were analyzed through thermal gravimetric (TG), differential thermal gravimetric (DTG) and differential scanning calorimetric (DSC) analysis. The FSsg and FSpp powders were characterized by X-ray powder diffraction (XRD) and atomic force microscopy (AFM). XRD reveals that the synthesized forsterite is of high crystallinity. As is evidenced by AFM, the average size of the nanoparticles is around 40 nm for FSsg and 30 nm for FSpp. The potential reaction mechanisms for the two synthesis routes were also established.