Recycling of plastic waste from electrical and electronic equipment (EEE), containing brominated flame retardants (BFR) remains difficult due to the increasingly stringent regulations on their handling and recovery. This report deals with photodegradation in a low-pressure reactor applying UV-visible light on Decabromodiphenyl ether (DBDE or BDE-209) randomly dispersed in commercially available Poly(acrylonitrile-butadiene-styrene) (ABS) and Poly(carbonate) (PC). The aim of this study is to investigate the possibility of decomposing a BFR in plastic waste from EEE while maintaining the specifications of the polymeric materials in order to allow for their recycling. The photodegradation of the extracted BFR was monitored using infrared spectroscopy and gas chromatography coupled with mass spectroscopy. DBDE underwent rapid photodegradation during the first minutes of exposure to UV-visible light and reached degradation yields superior to 90% after 15 min of irradiation. The evaluation of polymer properties (ABS and PC) after irradiation revealed superficial crosslinking effects, which were slightly accelerated in the presence of DBDE. However, the use of a low-pressure reactor avoids large photooxidation and allowed to maintain the thermal and structural properties of the virgin polymers.

The growing volume of plastics derived from electronic waste (e-waste) underscores the imperative for environmentally sustainable strategies for the management of this waste. In light of the paramount importance of this issue, a pilot demonstrator for the decontamination of polymers containing Brominated Flame Retardants (BFRs) has been developed. The objective is to investigate the potential for decontaminating BFR-containing polymers from e-waste via UV-visible irradiation using a rotatory laboratory pilot operating under primary vacuum conditions. This report focuses on binary model blends composed of 90 weight% (wt%) poly(Acrylo-Butadiene-Styrene) (ABS) pellets and 10 wt% Deca-Bromo-Diphenyl Ether (DBDE), which is one of the most toxic BFRs. The efficiency of the irradiation process was evaluated as a function of pellet diameter and irradiation time using Fourier Transform InfraRed spectroscopy (FTIR) and High-Resolution Laser Desorption/Ionization Mass Spectroscopy (HR-LDI-MS). As a consequence, ABS + DBDE achieved a decontamination efficiency of 97% when irradiated with pellets of less than 1 mm in diameter for a period of 4 h. Additionally, the thermal behavior of the irradiated samples was investigated through thermogravimetric analysis and differential scanning calorimetry. It was thus established that the application of UV-visible irradiation had no significant impact on the overall thermal properties of ABS.