Different ecological binders have been used to minimize the negative effects of cement production and use on the environment. Wood ash is one of these alternative binders, and there has been increasing research related to this topic recently. The wood ash utilized in the literature primarily originates from power plants and local bakeries, and predominantly wood fly ash is used. This review paper examines the use of wood ash as an ecological binder in two different applications: as a cement replacement and as an alkali-activated material. Studies have shown that while increased wood ash content in concrete and mortars can have negative effects on strength and durability, it is still a promising and developable material. Depending on the chemical composition of the wood ash, the strength and durability properties of concrete might be slightly improved by utilizing wood ash as a replacement for cement, with an optimal replacement level of 10–20%. However, there is a need for more research regarding the effects of wood ash on the durability of cement-based materials and its use in alkali-activated materials. Overall, this review provides a comprehensive overview of the properties of wood ash and its potential applications in conventional concrete and mortars, as well as in alkali-activated materials.

Cement production contributes significantly to carbon dioxide emissions. Alkali-activated materials offer an environmentally friendly alternative due to their comparable strength, durability and low-carbon emissions while utilizing wastes and industrial by-products. Wood ash is a waste material that shows promising results as a partial replacement for Portland cement and precursors in alkali-activated systems. The aim of this study was to examine the effect of ground wood ash on the mechanical properties of alkali-activated mortars. Wood ash was incorporated as a 0 wt%, 10 wt% and 20 wt% partial replacement for ground granulated blast furnace slag (GGBFS). The wood ashes were ground in a planetary ball mill for 10 and 20 min. Sodium silicate (Na₂SiO₃), sodium carbonate (Na₂CO₃), and sodium hydroxide (NaOH) were used as alkali activators. The results demonstrated that ground wood ash improved the mechanical properties of alkali-activated systems compared to untreated wood ash. However, the incorporation of wood ash increased the porosity of the binder matrix.

Wood ash is a promising supplementary cementitious material (SCM) due to its inherent pozzolanic properties. Intensive grinding has been shown to enhance this aspect and reduce the negative effects of variability in the chemical composition. This study investigated the influence of grinding through ball milling on the pozzolanic properties of wood ash. Four different types of wood ash were studied, each subjected to grinding durations of 10 and 20 min. Coal fly ash was used as a reference material. The pozzolanic activity of raw and ground wood ashes was evaluated using the strength activity index (SAI), the Frattini test, the R3 test, thermogravimetric analysis (TGA/DTG), X-ray diffraction (XRD) analysis, and scanning electron microscopy with energy-dispersive spectroscopy (SEM/EDS). The results indicated that both 10 min and 20 min grinding durations enhanced the reactivity and compressive strength. However, the 10 min grinding duration showed better overall performance than 20 min grinding, likely due to reduced agglomeration and more effective particle refinement. For calcium-rich wood ashes, the reactivity was linked to the hydraulic properties rather than the pozzolanic properties.