The influence of fiber orientation on the mechanical behavior of a polymer matrix composite reinforced with natural jute fibers is investigated in this study. Two fiber orientation configurations are examined: the first involves woven fibers aligned in the direction of testing, while the second considers a 45° orientation. The research involves manufacturing composite plates using jute fabric with the mentioned orientations, followed by cutting rectangular specimens for tensile testing to determine which orientation yields superior properties. Displacement fields are measured using a digital image correlation technique, synchronized with load data obtained from a universal testing machine equipped with a load cell to obtain stress–strain curves for each configuration. Results indicate that 0° specimens achieve higher stress but lower strain compared to 45° specimens. This research contributes to understanding the optimal fiber alignment for enhancing the mechanical performance of fiber-reinforced polymer composites.

The present work reports a comparative study of ductile failure models applied to an Al-2011 aluminum alloy single-pass wire drawing process using different reductions. The material damage experienced in the wire after passing through the die is evaluated using the well-known Rice and Tracey, Cockcroft and Latham, Brozzo and Modified Chaouadi models. Due to the fact that nonrealistic damage predictions are found for the highest studied wire reduction, an alternative uncoupled failure criterion combining the effect of deformation and triaxility is proposed. The ability of these five models in predicting the formation of chevrons in the process is the main focus of this research. First, the model parameters are characterized by means of numerical simulations of the tensile test. Then, the predictions of the numerical analyses of the drawing process are compared with available experimental results where physical evidence of chevrons was found. Relevant variables are analyzed to determine their incidence in the formation of central bursts. Finally, the performance of this new model is assessed for the full reduction scenarios.

The influence of the addition of bentonite nanoparticles on the tensile and flexural strength of a thermosetting polymer matrix composite material reinforced with hemp fibers was de-terminated. All composites were manufactured with 5% of bentonite in the polymer mass–weight ratios and 10 to 45 wt% of fibers with a step of 5%. For mechanical characterization, tensile and flexural tests were performed: scanning electron microscopy and energy-dispersive X-ray spectroscopy analyses were carried out. The tensile strength of the samples containing bentonite compared to the polymer samples with the fiber addition was affected for all fiber addition percentages, except for 35% while the flexural resistance improved with the addition of bentonite in the percentages of 20, 30, 35, and 45% of fiber addition. With the addition of bentonite, the maximum values of tensile and flexural strength were both obtained for the 35% addition of fibers, with values of 34.28 MPa and 98.04 MPa, respectively. The presence of bentonite favored the rigidity of the material to traction and bending, which was reflected through an increase in the elastic modulus compared to the composite that only had fiber. The maximum values obtained were 9065 MPa in tension and 8453 MPa in flexion for the 40% and 35% of addition of fiber, respectively. Microscopy showed a good distribution of fibers in the matrix, the absence of internal porosities, and a good interaction between matrix and reinforcement.

Composites with natural lignocellulosic fillers are being cited as a viable and sustainable alternative to conventional materials, as they combine lower costs with lower weight. In many tropical countries, such as Brazil, there is a considerable amount of lignocellulosic waste that is improperly discarded, which causes pollution of the environment. The Amazon region has huge deposits of clay silicate materials in the Negro River basin, such as kaolin, which can be used as fillers in polymeric composite materials. This work investigates a new composite material (ETK) made of epoxy resin (ER), powdered tucumã endocarp (PTE), and kaolin (K), without coupling agents, with the aim of producing a composite with lower environmental impact. The ETK samples, totaling 25 different compositions, were prepared by cold molding. Characterizations of the samples were performed using a scanning electron microscope (SEM) and a Fourier-transform infrared spectrometer (FTIR). In addition, the mechanical properties were determined via tensile, compressive, three-point flexural and impact tests. The FTIR and SEM results showed an interaction between ER, PTE, and K, and the incorporation of PTE and K reduced the mechanical properties of the ETK samples. Nonetheless, these composites can be considered potential materials to be used for sustainable engineering applications in which high mechanical strength is not a main requirement of the material.

As a part of the mission to create materials that are more environmentally friendly, we present the following proposal, in which a study of the mechanical properties of composite materials comprising a polyester resin with sisal fiber and bentonite particles was conducted. Sisal fiber was added to a matrix in percentages ranging from 5% to 45% in relation to the polyester resin weight, while bentonite remained fixed at 7% in relation to the polyester resin weight. The specimens were manufactured by compression molding. The mechanical properties were analyzed by tensile, bending, impact, stepped creep, and relaxation tests. In addition, energy-dispersive X-ray spectroscopy and scanning electron microscopy analyses were carried out to analyze the composition and heterogeneity of the structure of the composite material. The results obtained showed that 7% of bentonite added to the matrix affects the tensile strength. Flexural strength increased by up to 21% in the specimens with a 20% addition of sisal fiber, while the elastic modulus increased by up to 43% in the case of a 20% addition of sisal fiber. The viscoelastic behavior was improved, while the relaxation stress was affected.

This paper presents an experimental and numerical analysis of damage evolution in AA2011 aluminum alloy wires drawn under different scenarios. To this end, load-unload tensile tests were firstly carried out in order to characterize the degradation of the mechanical response in every cycle where the experimental results show a bilinear damage relationship in terms of the effective plastic strain. Therefore, a modification of the classical Lemaitre model is proposed in this work in order to reproduce bilinear paths of damage with the addition of only two parameters that can be directly obtained from the material characterization. Then, the damage predictive capability of this new experimental-based model is assessed in numerical simulations of the drawing process in one and two passes (considering for this last case the sequential and tandem configurations) where the computed predictions are compared with the corresponding experimental data showing a good agreement between them.