The aim of this work is to analyze the effect of water absorption on the mechanical properties and damage mechanisms of polyester/glass fiber/jute fiber hybrid composites obtained using the compression molding and vacuum-assisted resin transfer molding (VARTM) techniques with different stacking sequences. For this purpose, the mechanical behavior under tensile stress of the samples was evaluated before and after hygrothermal aging at different temperatures: TA, 50 °C, and 70 °C for a period of 696 h. The damage mechanism after the mechanical tests was evaluated using SEM analysis. The results showed a tendency for the mechanical properties of the composites to decrease with exposure to an aqueous ambient, regardless of the molding technique used to conform the composites. It was also observed that the stacking sequence had no significant influence on the dry composites. However, exposure to the aqueous ambient led to a reduction in mechanical properties, both for the molding technique and the stacking sequence. Damage such as delamination, fiber pull-out, fiber/matrix detachment, voids, and matrix removal were observed in the composites in the SEM analyses.

The influence of fiber orientation on the mechanical behavior of a polymer matrix composite reinforced with natural jute fibers is investigated in this study. Two fiber orientation configurations are examined: the first involves woven fibers aligned in the direction of testing, while the second considers a 45° orientation. The research involves manufacturing composite plates using jute fabric with the mentioned orientations, followed by cutting rectangular specimens for tensile testing to determine which orientation yields superior properties. Displacement fields are measured using a digital image correlation technique, synchronized with load data obtained from a universal testing machine equipped with a load cell to obtain stress–strain curves for each configuration. Results indicate that 0° specimens achieve higher stress but lower strain compared to 45° specimens. This research contributes to understanding the optimal fiber alignment for enhancing the mechanical performance of fiber-reinforced polymer composites.

The aim of this work is to analyze water sorption in hybrid polyester/glass fabric/jute fabric composites molded via compression and VARTM (Vacuum-Assisted Resin Transfer Molding). The laminates were produced with five different stacking sequences and subjected to water sorption testing at room temperature, 50 °C and 70 °C. This study consisted of two stages: experimental and theoretical stages. The composites had a fiber volume content ranging from 30% to 40%. Water absorption and diffusion coefficient in the hybrid composites were intermediate to those reinforced with a single type of fiber. There were no significant differences in these properties based on fiber arrangement once the composites reached saturation. Diffusion coefficient values were higher for specimens with jute fiber on at least one of the outer surfaces. Water sorption rates increased with higher immersion temperatures. The water sorption at saturation point was not affected by the manufacturing process. Among the hybrid composites, those with jute on the surfaces showed the highest diffusion coefficient, while those with glass on the surface had the lowest values. Higher diffusion coefficient values were observed at temperatures of 50 °C and 70 °C. The main influencing factors on the absorbed moisture content for composites are the presence and content of jute fibers in the system and the immersion temperature. The manufacturing process does not affect the water sorption at saturation point.