A novel tungsten disulfide-molybdenum copper oxide composite supported with graphene quantum dots (WM@GQDs) has been synthesized as a counter electrode (CE) for dye-sensitized solar cells (DSSCs) using a simple and low-cost ultrasonication method. The unique structure of WM@GQDs exhibits excellent power conversion efficiency due to its high catalytic activity and charge transport properties. In addition, the graphene quantum dots (GQDs) provide more active sites in the zero-dimensional materials for an I/I₃⁻ redox reaction which can improve the electrical and optical properties of the composite. The results indicate that the amount of GQDs in the composite affect the effectiveness of solar devices. When 0.9%wt of GQDs was used, the WM@GQDs composite achieved an efficiency of 10.38%, which is higher than that of the expensive platinum CE under the same conditions. The mechanism behind the improved power conversion efficiency (PCE) of the composite sample is also discussed in detail. Therefore, WM@GQDs can be an efficient material to replace platinum in DSSCs as a CE.

To address the issues associated with traditional counter electrodes, a novel gamma-irradiated chitosan-doped reduced graphene-CuInS₂ composite (Chi@RGO-CIS) was used as the counter electrode (CE).

Novel MoWO₄ with ZnO nanoflowers was synthesized on multi-walled carbon nanotubes (MW-Z@MWCNTs) through a simple hydrothermal method, and this unique structure was applied as a counter electrode (CE) for dye-sensitized solar cells (DSSC) for the first time. The synergetic effect of ZnO nanoflowers and MoWO₄ on MWCNTs was systematically investigated by different techniques. The amount of MWCNTs was optimized to achieve the best DSSC performance. It was found that the 1.5% MW-Z@MWCNTs composite structure had the highest power conversion efficiency of 9.96%, which is greater than that of traditional Pt CE. Therefore, MW-Z@MWCNTs-based CE can be used to replace traditional Pt-based electrodes in the future.

A large amount of agricultural waste was used to prepare cellulose (Cel) and then the surface was modified with PEI (Cel-PEI) using the microwave method. To be used as a metal adsorbent, the adsorption of Cr (VI) from an aqueous solution by Cel-PEI was measured using Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), X-ray diffraction (XRD), and thermogravimetric analysis (TGA) techniques. The parameters of Cr (VI) adsorption in solution by the Cel-PEI adsorbent were as follows: the pH of the solution was 3, the concentration of the chromium solution was 100 mg/L, and the adsorption time was 180 min at 30 °C using 0.01 g of adsorbent. Cel-PEI had a Cr (VI) adsorption capacity of 106.60 mg/g, while the unadjusted Cel was 23.40 mg/g and the material recovery showed a decrease in efficiency of 22.19% and 54.27% in the second and third cycles, respectively. The absorption isotherm of chromium adsorption was also observed. The Cel-PEI material conformed to the Langmuir model with an R² value of 0.9997. The kinetics of chromium adsorption showed that under pseudo-second-order analysis, with R² values of 0.9909 and 0.9958 for Cel and Cel-PEI materials, respectively. The G° and H° values of the adsorption process were negative, indicating that the adsorption is spontaneous and that the adsorption process is exothermic. The efficient preparation adsorbent materials for Cr (VI) was achieved using a short microwave method that is low-cost and environmentally friendly for use in the treatment of Cr-contaminated wastewater.