With the rise in the demand for eco-friendly and electric vehicles, welding and heat treatment are becoming very important to meet the necessary weight reduction, complexity, and high functionality of die castings. Pore-free (PF) die casting is an effective process that enables heat treatment and welding due to low gas porosities. Indeed, this process affords castings of low gas porosity, similar to those attained by high-vacuum die casting. In this study, we compared the gas porosities of different castings fabricated by PF die casting using varied injected oxygen amounts. The castings were all subjected to T6 heat treatment and analyzed by computed tomography (CT) to compare their microstructure and mechanical properties before and after T6 heat treatment. The results revealed that with the increasing injected oxygen amount, the gas porosity of the specimens decreased while their mechanical properties increased. In particular, the gas porosity was the lowest at 1.26 L. Moreover, the 1.26 L specimen displayed the best tensile strength, yield strength, and elongation results. Finally, Weibull distribution analysis revealed that the tensile strength and elongation repeatability and reproducibility increased with increasing injected oxygen amount.

A383 Al-Si-Cu alloy matrix composites were reinforced with different amounts (0.5, 1.0, 1.5 and 2.0 wt%) of chopped multiwalled carbon nanotubes (MWCNTs) and fabricated using the oxygen-replacing die casting (ORDC) process to reduce gas porosities via the reaction of molten Al and O₂ replaced in the mold cavity. MWCNTs were added to the mold cavity by supplying O₂ and using a poly gate in the ORDC mold to improve CNT dispersity in the matrix of the composite. Microstructure studies of the composites showed a uniform CNT distribution within the matrix and grain refinement. X-ray computed tomography images showed that the internal porosities were affected by the CNT addition amount and gate type used in the mold, and Raman spectroscopy analysis indicated that CNTs in the matrix were free of significant defects. The 1.0 wt% CNT-added composite cast using the poly gate showed the highest ultimate tensile strength of 258.5 ± 5.2 MPa and hardness of 157.9 ± 3.0 Hv; these values were, respectively, 21% and 30% higher than those of the monolithic A383 alloy, confirming the feasibility of fabricating the MWCNT-added A383 alloy composite with a poly gate using the ORDC process.