Wood plastic composite (WPC) usage and demand have increased because of its interesting chemical and mechanical properties compared to other plastic materials. However, there is a possibility of structural and mechanical changes to the material when exposed to the external environment; most research on wood plastic is performed on the material with elevated fiber content (40–70%). Therefore, more research needs to be performed regarding these issues, especially when the fiber content of the WPC is low. In this study, composite materials composed of high-density polyethylene (HDPE) reinforced with yellow birch fibers (20 and 30%) were made by injection molding. The fibers were treated with dissolved zinc oxide (ZnO) powder in sodium oxide (NaOH) solution, and the fabricated material was exposed to fungal rot. ZnO treatment in this case is different from most studies because ZnO nanoparticles are usually employed. The main reason was to obtain better fixation of ZnO on the fibers. The mechanical properties of the composites were assessed by the tensile and Izod impact tests. The impact energies of the samples fabricated with ZnO-treated fibers and exposed to Gloephyllum trabeum and Trametes versicolor decreased, when compared to samples fabricated with ZnO-nontreated fibers. The mechanical properties of the samples composed of ZnO-treated fibers and exposed to rot decreased, which were reported by a decreased Young’s modulus and impact energies. The usage of ZnO treatment prevented mycelium proliferation, which was nonexistent on the samples. It has been noted that the decrease in mechanical properties of the treated samples was because of the action of NaOH used to dissolve the ZnO powder.

Wood plastic composite usage and demands have increased due to chemical, and mechanical properties when compared to plastic materials. However, because of the possibility of structural and mechanical changes of the material when exposed to external environment more research needs to be done. In the present study yellow birch/HDPE composites materials made by injection molding were treated by zinc oxide and exposed to fungal rots. Mechanical properties of the composites were assessed by Tensile and Izod impact test. The impact energies of the samples loaded with 30 % ZnO-treated fibers and exposed to G. trabeum and T. versicolor decreased, compared to when samples were not treated with ZnO. The mechanical properties of all samples treated with ZnO and exposed to rot decreased which were reported as a decreased Young's modulus and impact energies. ZnO prevented mycelium proliferation which was nonexistent on samples. It has been noted that the decrease in mechanical properties of treated samples was due to NaOH used to dissolve the ZnO powder.