Polyester/polyamide 6 hollow segmented pie bicomponent spunbond hydro-entangled microfiber nonwovens (PET/PA6) with a microfilament structure have recently emerged in many markets around the world due to their green, high-strength, and lightweight properties. However, PET/PA6 is highly hydrophobic, which inhibits its large-scale application at present. In order to enhance the hydrophilic performance of PET/PA6, many methods have been applied, but the effects are not obvious. Ultraviolet (UV) irradiation treatment has proven to be an effective method to improve the hydrophilicity of fabrics. Herein, the aim of this paper was to investigate hydrophilic modification of PET/PA6 by UV/TiO₂/H₂O₂. The effect of H₂O₂, nano-TiO₂, and UV irradiation time on the morphology, elemental composition, hydrophilic properties, and mechanical properties of PET/PA6 were systematically investigated. The results showed that the modified microfibers were coated with a layer of granular material on the surface. It was found that the C 1s peak could be deconvoluted into six components (C–C–C, C–C–O, O–C=O, N–C=O, N–C–C, and C–C=O), and a suitable mechanism was proposed. Moreover, the water contact angle of PET/PA6 modified by 90 min irradiation with UV/TiO₂/H₂O₂ decreased to zero in 0.015 s, leading to the water vapor transmission rate and the water absorption reaching 5567.49 g/(m²·24 h) and 438.81%, respectively. In addition, the modified PET/PA6 had an excellent liquid wicking height of 141.87 mm and liquid wicking rate of 28.37 mm/min.

PET/PA6, hollow, segmented-pie, microfiber nonwovens (PET/PA6 HSMNs) play an important role in a microfiber, synthetic leather base. Most of the current PET/PA6 HSMNs generally lack in hygiene performance. Moreover, there is an urgent need for the asymmetric wettability of PET/PA6 HSMNs to ensure the comfort of clothing. In this work, a novel, asymmetrically wettable, PET/PA6 HSMN with a gradient structure is proposed, which can regulate liquid adsorption and directional transport. An MOF-303 was successfully synthesized and loaded onto the PET/PA6 HSMN, which had been pre-treated with gradient hydrolysis under sulfuric acid. The droplet quickly permeated the modified PET/PA6 HSMN, and the droplet disappearance time decreased to 62.40 ms. The liquid strikethrough time of the modified PET/PA6 HSMN reached 5.16 s. The maximum adsorption capacity of the modified PET/PA6 HSMN was 68.161 mg/g, which was improved by 122.83%. In addition, the air permeability of the pre-treated PET/PA6 HSMN increased from 308.70 mm/s to 469.97 mm/s, with the sulfuric acid concentrations increasing from 0% to 20%, and the air permeability of the modified PET/PA6 HSMN decreased gradually from 247.37 mm/s to 161.50 mm/s. Furthermore, the tensile strength of the modified PET/PA6 HSMN treated with sulfuric acid and MOF-303 was also obviously enhanced compared with the PET/PA6 HSMN treated with pure sulfuric acid. This PET/PA6 HSMN, with asymmetric wettability, owing to its high hygiene performance and water transport capabilities, is promising and able to extend the application of a microfiber synthetic leather base for clothing.