In this study, the ballistic performance of armors composed of a polyurea elastomer/Kevlar fabric composite and a shear thickening fluid (STF) structure was investigated. The polyurea used was a reaction product of aromatic diphenylmethane isocyanate (A agent) and amine-terminated polyether resin (B agent). The A and B agents were diluted, mixed and brushed onto Kevlar fabric. After the reaction of A and B agents was complete, the polyurea/Kevlar composite was formed. STF structure was prepared through pouring the STF into a honeycomb paper panel. The ballistic tests were conducted with reference to NIJ 0101.06 Ballistic Test Specification Class II and Class IIIA, using 9 mm FMJ and 44 magnum bullets. The ballistic test results reveal that polyurea/Kevlar fabric composites offer better impact resistance than conventional Kevlar fabrics and a 2 mm STF structure could replace approximately 10 layers of Kevlar in a ballistic resistant layer. Our results also showed that a high-strength composite laminate using the best polyurea/Kevlar plates combined with the STF structure was more than 17% lighter and thinner than the conventional Kevlar laminate, indicating that the high-strength protective material developed in this study is superior to the traditional protective materials.

In this study, the impact resistance of aramid fabric reinforced with shear thickening fluids (STFs), epoxy or polyurea elastomers is examined through ballistic tests. According to the ballistic test results, the aramid composite structure treated with polyurea elastomers absorbs the most impact energy per unit area density and has the best impact resistance. However, the occurrence of stress concentration during ballistic impact reduces the impact resistance of the aramid composite structure treated with epoxy. On the other hand, aramid fabric impregnated with STF improves structural protection, but it also increases the weight of the composite structure and reduces the specific energy absorption (SEA). The results of this study analyze the energy absorption properties, deformation characteristics, and damage modes of different aramid composites, which will be of interest to future researchers developing next-generation protective equipment.