In this study, a thorough investigation of the microstructures and tensile properties of 316L stainless steel fabricated via laser powder bed fusion (L-PBF) was done. 316L stainless steel specimens with two different thicknesses of 1.5 mm and 4.0 mm fabricated under similar conditions were utilized. Microstructural characterization was performed using optical microscopy (OM) and scanning electron microscopy (SEM) equipped with electron backscatter diffraction (EBSD). Melt pools and cellular structures were observed using OM, whereas EBSD was utilized to obtain the grain size, grain boundary characteristics, and crystallographic texture. The 1.5 mm thick sample demonstrated a yield strength (YS) of 538.42 MPa, ultimate tensile strength (UTS) of 606.47 MPa, and elongation to failure of 69.88%, whereas the 4.0 mm thick sample had a YS of 551.21 MPa, UTS of 619.58 MPa, and elongation to failure of 73.66%. These results demonstrated a slight decrease in mechanical properties with decreasing thickness, with a 2.4% reduction in YS, 2.1% reduction in UTS, and 5.8% reduction in elongation to failure. In addition to other microstructural features, the cellular structures were observed to be the major contributors to the high mechanical properties. Using the inverse pole figure (IPF) maps, both thicknesses depicted a crystallographic texture of {001} in their as-built state. However, when subjected to tensile loads, texture transitions to {111} and {111} were observed for the 1.5 mm and 4.0 mm samples, respectively. Additionally, EBSD analysis revealed the pre-existence of high-density dislocation networks and a high fraction of low-angle grain boundaries. Interestingly, twinning was observed, suggesting that the plastic deformation occurred through dislocation gliding and deformation twinning.

This study investigated the fatigue performance of 316L stainless steel fabricated via laser powder bed fusion (LPBF). Stress-controlled fatigue tests were performed at different stress amplitudes on vertically built samples using a frequency of 15 Hz and a stress ratio of 0.1. The stress amplitudes were varied to provide the cyclic response of the materials under a range of loading conditions. The average fatigue strength was determined to be 92.94 MPa, corresponding to a maximum stress of 185.87 MPa. The microstructures were observed through scanning electron microscopy (SEM) with the aid of electron backscattered diffraction (EBSD), and the average grain size of the as-built samples was determined to be 15.6 µm, with most grains having a preferred crystallographic orientation. A higher kernel average misorientation value was measured on the deformed surfaces, revealing the increased misorientation of the grains. Defects were observed on the fractured surfaces acting as crack initiators while deflecting the crack propagation paths. The fatigue failure mode for the LPBF 316L samples was ductile, as illustrated by the numerous dimples on fracture surfaces and fatigue striations.