As a promising alternative to traditional prepreg, carbon fiber/poly(ether ether ketone) (CF/PEEK) hybrid composites have attracted wide public interest for their flexibility and conformability. However, modification methods focused on the hybrid premix have not been previously studied. In the present work, the interfacial strength of the hybrid composite was improved by treating the carbon and PEEK fibers together in a radiofrequency (RF) plasma containing one of the following gases to achieve surface activation: air, Ar, or Ar–air. After plasma treatment, the increased roughness of CF and the grafted chemical groups of CFs and PEEK fibers were propitious to the mechanical interlocking and interfacial strength. Significant interfacial shear strength (IFSS) enhancement was achieved after Ar 1 min, air 1 min plasma treatment. This study offers an alternative method for improving the interfacial properties of CF/PEEK composites by focusing on the boundary layer and modifying and controlling the fiber–matrix interface.

Transdermal drug delivery is a new means of delivering drugs through the skin to achieve therapeutic effects. Microneedles have several advantages, including low cost, easy self-administration, and high delivery efficiency. Different polymers affect the morphology, mechanical properties, and drug delivery efficiency of microneedles. To study the performance and limitations of microneedles (MNs), we prepared different ratios of polymers. MNs were fabricated from polyvinylpyrrolidone (PVP) and sodium carboxymethyl cellulose (CMC-Na) using the centrifugal molding method. Needle morphology, formability, and other properties of the polymers were evaluated to compare the performances of MNs with different ratios. PVP and CMC-Na were intermixed at different ratios with water as the solvent. The soluble MNs were prepared by mold casting. The morphology, thermodynamic properties, and crystallinity were studied using scanning electron microscopy (SEM), thermogravimetric analysis (TG), differential scanning calorimetric analysis (DSC), and X-ray diffraction (XRD). The results showed that composite microneedles have good thermal stability. Among the different compositions tested, the 10% PVP/2% CMC-Na composite microneedle demonstrated the best performance with a regular surface morphology and relatively high thermal decomposition and melting temperatures. These results indicate that microneedles with appropriate ratios of two different materials possess good formability and other properties.

Developing scaffolds with appropriate mechanical/structural features as well as tunable bioactivities are indispensable in the field of tissue engineering. This study focused on one such attempt to electrospin the copolymer of L-lactic acid (L-LA) and functional monomer (3(S)- [(benzyloxycarbony)methyl]-1,4-dioxane-2,5-dione, BMD) with small peptide modifications for the purpose of neural tissue engineering. Scanning Electron Microscopy (SEM) micrographs showed fabricated electrospun copolymer as porous and uniform nanofibrous materials with diameter in the range of 800–1000 nm. In addition, the modified scaffolds displayed a lower contact angle than poly(L-lactide) (PLLA) indicating higher hydrophilicity. To further incorporate the bioactive functions, the nanofibers were chemically coupled with small peptide (isoleucine-lysine-valine-alanine-valine, IKVAV). The incorporation of IKVAV onto the electrospun fiber was confirmed by X-ray photoelectron spectroscopy (XPS) and such incorporation did not affect the surface morphology or fiber diameters. To demonstrate the potential of applying the designed scaffolds for nerve regeneration, dorsal root ganglion (DRG) neurons were cultured on the nanofibers to examine the impact on neurite outgrowth of DRGs. The results indicated that the fabricated nanofibrous matrix with small peptide might be a potential candidate for neural tissue engineering.

As a favorable hydrophilic additive for antifouling modification of polyvinylidene fluoride (PVDF) membrane, titanium dioxide (TiO₂) nanoparticles have been applied for years. Sodium dodecyl sulfonate (SDS), a representative anionic surfactant, has been proven to benefit the dispersion of nano-TiO₂ via an electro-spatial stabilizing mechanism. In this study, various proportionally SDS-functionalized TiO₂ nanoparticles were adopted to modify PVDF membrane. Dispersion and stability of SDS-functionalized TiO₂ nanoparticles in casting solutions were evaluated by multiple light scattering technology. The properties and antifouling performance of PVDF/SDS-TiO₂ composite membranes were assessed. The uniformity of surface pores as well as structures on cross-section morphologies was modified. The finger-like structure of PVDF/SDS-TiO₂ composite membrane was adequately developed at the SDS/TiO₂ mass ratio of 1:1. The improved antifouling performance was corroborated by the increasing free energy of cohesion and adhesion as well as the interaction energy barrier between membrane surfaces and approaching foulants assessed by classic extended Derjaguin–Landau–Verwey–Overbeek (XDLVO) theory, the low flux decline during bovine serum albumin (BSA) solution filtration process, and the high critical flux (38 L/(m²·h·kPa)) in membrane bioreactor. This study exploits a promising way to modify PVDF membrane applicable to the wastewater treatment field.