As a promising alternative to traditional prepreg, carbon fiber/poly(ether ether ketone) (CF/PEEK) hybrid composites have attracted wide public interest for their flexibility and conformability. However, modification methods focused on the hybrid premix have not been previously studied. In the present work, the interfacial strength of the hybrid composite was improved by treating the carbon and PEEK fibers together in a radiofrequency (RF) plasma containing one of the following gases to achieve surface activation: air, Ar, or Ar–air. After plasma treatment, the increased roughness of CF and the grafted chemical groups of CFs and PEEK fibers were propitious to the mechanical interlocking and interfacial strength. Significant interfacial shear strength (IFSS) enhancement was achieved after Ar 1 min, air 1 min plasma treatment. This study offers an alternative method for improving the interfacial properties of CF/PEEK composites by focusing on the boundary layer and modifying and controlling the fiber–matrix interface.

Continuous carbon fiber (CF)-reinforced poly (ether ether ketone) (PEEK) composites have excellent mechanical properties, but their processing techniques are limited. Therefore, we promoted a braiding method based on the hybrid fiber method by hot-compacting CF/PEEK plain weave fabrics to solve the problem of difficult wetting between CF and PEEK. Four parameters—melting temperature, molding pressure, crystallization temperature and the resin contents—were investigated for optimized fabrication. After studying the melting range, thermal stability and the contact angle of PEEK under different temperatures, the melting temperature was set at 370 °C. An ultra-depth-of-field 3D microscope was adopted to investigate the effects of molding pressure in the melting stage. The tensile strength or modulus along and perpendicular to the carbon fiber direction and crystallinity under different crystallization temperatures were analyzed. As a result, the sample crystalized at 300 °C showed an excellent tensile properties and crystallinity. The increased mass ratio of PEEK ranging from 50.45% to 59.07% allowed for much stronger interfacial strength; however, the higher resin content can lead to the dispersion of CFs, loss of resin and the formation of defects during processing. Finally, the optimal resin mass content was 59.07%, with a tensile strength of 738.36 ± 14.49 MPa and a flexural strength of 659.68 ± 57.53 MPa. This paper studied the optimized processing parameters to obtain better properties from CF/PEEK plain weave fabrics and to further broaden the specific applications of CF/PEEK composites, demonstrating a new direction for its fabrication.

Blends of cyanate ester and phthalonitrile–polyhedral oligomeric silsesquioxane copolymers were prepared, and their cure behavior and properties were compared via differential scanning calorimetry (DSC) analysis, thermogravimetric (TG) analysis, dynamic mechanical analysis, Fourier-transform far-infrared (FTIR) spectroscopy, and rheometric studies. The copolymer blends showed high chemical reactivity, low viscosity, and good thermal stability (TG temperatures were above 400 °C). The glass-transition temperature of the blends increased by at least 140 °C compared to cyanate ester resin. The blends are suitable for preparing carbon-fiber-reinforced composite materials via a winding process and a prepreg lay-up process with a molding technique. The FTIR data showed that the polymerization products contained triazine-ring structures that were responsible for the superior thermal properties.