Oral rehabilitation with dental implants has revolutionized the field of dentistry and has been proven to be an effective procedure. However, the incidence of peri-implantitis has become an emerging concern. The efficacy of the decontamination of the implant surface, by means of lasers, is still controversial. Previous studies have revealed a reduction in osteoblast adhesion to carbon-contaminated implant surfaces. This in-vitro study aimed to evaluate the decontamination of failed implants by assessing the carbon proportion, after irradiation by low-energy erbium yttrium-aluminum-garnet laser (Er:YAG) (Fotona; 2940 nm, Ljubljana, Slovenia) for a single and for multiple passages, until getting a surface, free of organic matters; to find the appropriate procedure for dental-implant surface-decontamination. Ninety implants were used. Thirty sterile implants were kept as a negative control. Thirty failed implants were irradiated by the Er:YAG laser, for a single passage, and the other thirty, for multiple passages. The parameters used in our experiments were an irradiation energy of 50 mJ, frequency of 30 Hz, and an energy density of 3.76 J/cm². A sapphire tip, with a length of 8 mm, was used with concomitant water spray irrigation, under air 6 and water spray 4. Super short pulse mode (SSP) was of 50 μs; irradiation speed being 2 mm/s. We used energy-dispersive X-ray spectroscopy (EDX) to evaluate the carbon proportion on the surfaces of the sterile implants, the contaminated, and the lased implants, with one (LX1) and with three passages (LX3). Statistical analysis was performed by ANOVA. Results showed mean difference between the three groups (contaminated, LX1, and LX3) with p < 0.0001, as between LX1 and Group A (p < 0.0001), while the difference between LX3 and the control group was not statistically significant. The decontamination of the implant surfaces with a low-energy Er:YAG laser with three passages, appeared to be an encouraging approach.

The discomfort of patients due to dentinal hypersensitivity (DH) is one of the main challenges that dentists face in daily practice. Difficulties in DH treatment gave rise to many protocols which are currently used. The aim of this clinical study is to evaluate the effectiveness of a new protocol on the reduction of dentinal hypersensitivity with diode laser 980 nm and the application of a graphite paste. 184 patients enrolled in the study, the degree of pain was evaluated by visual analog scale (VAS), graphite paste was applied on the exposed dentine before irradiation, the application of diode laser 980 nm with continuous mode, backward motion, tangential incidence of the beam in non-contact mode and a delivery output of 1 W. Fiber’s diameter was 320 μm and total exposure time depended on the time necessary to remove the graphite paste from the teeth. Statistical analyses were performed with Prism 5^® software. Pain in post-operative significantly decreased immediately after the treatment. Mean values stayed stable until a 6-month follow-up. The application is considered to be safe with long-term effectiveness.

In the last decade, the success of lasers in simplifying many dental procedures has heightened the need for research in the orthodontic field, in order to evaluate the benefits of laser-assisted ceramic brackets debonding. Conventional ceramic brackets removal delivers a high shear bond strength (SBS), which might lead to enamel damage. Nowadays, debonding ceramic brackets by Er:YAG laser seems a viable alternative technique; however, there is no data on the use of Er,Cr:YSGG in the literature. We aimed to evaluate the difference in enamel topography derived from different erbium laser settings used during debonding. One hundred and eighty bovine incisors teeth were randomly divided into fifteen experimental groups, according to different erbium laser settings using scanning methods. SBS testing was performed after debonding; stereomicroscopic and SEM analyses were done after cleaning the remaining adhesive so as to assess the incidence of enamel microcracks formation and enamel loss. There were no statistically significant differences between the proportions of teeth with normal enamel topography within the control group when compared with any of the Er:YAG groups. However, the proportion of teeth with a normal enamel topography in Er,Cr:YSGG was 4 W/20 Hz (83.3%) and in Er:YAG was 5 W/20 Hz (91.7%), which was statistically significantly higher than the control group (41.7%). The selection of erbium lasers’ optimal parameters during debonding influences the enamel topography. When considering the evaluation of both microscopic and statistical analyses, irradiation by Er:YAG (120 mJ/40 Hz) displayed a significant reduction in microcracks compared with conventional debonding, even though some microstructural changes in the enamel could be noted. Er,Cr:YSGG (4 W/20 Hz) respected the enamel topography the most out of the studied groups.

Introduction. The aim of this study was to assess the complications resulting from third molar extraction under general anesthesia.Material and Methods. The retrospective study included all patients who underwent impacted third molars extraction from January 2008 until December 2011. 7659 third molars were extracted for 2112 patients. Postoperative complications were retrieved from medical files.Results. No complications were related to general anesthesia. The most frequent postoperative complication was infection (7.15%). Lingual nerve injuries affected 1.8% of the patients. All of them were transient and were not related to tooth section. Inferior alveolar nerve injuries were reported in 0.4% of the cases. 95.8% of these patients were admitted for one-day ambulatory care, and only two patients were readmitted after discharge from hospital.Discussion. This surgical technique offers comfort for both surgeons and patients. Risks are only linked to the surgical procedure as we observed no complication resulting from general anesthesia. One-day hospitalization offers a good balance between comfort, security, and cost. The incidence of complications is in agreement with the literature data, especially regarding pain, edema, and infectious and nervous complications. It is of utmost importance to discuss indications with patients, and to provide them with clear information.

Objective. To investigate the shear bond strength of self-adhering flowable resin composite, to dentin, after exposing it to Er:YAG laser radiation, at different energy densities.Materials and Methods. Sixty freshly extracted human third molars were randomly divided into five groups (n=12). In the control group, dentin was left unirradiated, whereas, in the other four groups, dentin was irradiated with Er:YAG laser in noncontact mode (MSP mode = 100 µs; 10 Hz; beam diameter: 1.3 mm; speed of 1 mm/second; air 6 mL/min; and water 4 mL/min), and respectively, with the following level of energy (50 mJ, 60 mJ, 80 mJ, and 100 mJ). Then, self-adhering flowable resin composite was bonded to all prepared dentin surfaces. Shear bond strength (SBS) was applied and fractured surfaces were examined using scanning electron microscopy.Results. SBS values showed significant differences in 60 mJ (P<0.05) compared to other groups. Morphological evaluation revealed tags or plugs in dentinal tubules, especially when 60 mJ and 80 mJ were used. All four groups tended to leave more residues on the dentin surface, than the control group.Conclusion. Er:YAG dentin irradiation may enhance SBS of the self-adhering flowable resin composite when it is used at the appropriate low level of energy density.

(1) Background: Bonding composite to tooth structure is still evolving with a substitute for phosphoric acid being the main challenge. Lately, a self-adhering composite (SAC) was developed, promising to simplify bonding to tooth structure. Unfortunately, retention especially to dentin, was not as good as the gold standard three steps bonding system. During the last 2 decades, lasers were used to enhance shear bond strength of composite to tooth structure. However, the literature provided limited information regarding laser efficiency in the immediate, as well as the long term, adhesion success of SACs to dentin. The purpose of our study was to define the optimal irradiation conditions to improve the adhesion of self-adhering flowable resin composite to dentin exposed to Er:YAG and Er,Cr:YSGG laser irradiation. (2) Methods: Seventy-two freshly extracted human third molars, prepared to have flat dentinal surfaces, were randomly divided into three groups (n = 24) including a control group (Group 1) in which dentin was left without laser irradiation. The other two groups (Group 2 and 3) received standardized irradiation at a speed of 1 mm/second with Er:YAG (60 mJ; SSP mode = 50 μs; 10 Hz; fluency of 9.4 J/cm²; beam diameter: 0.9 mm; air 6 mL/min; and water 4 mL/min), and Er,Cr:YSGG: 1.5 W; fluency of 17.8 J/cm²; turbo handpiece with MX5 short insert; 20 Hz under air/water spray (65% air, 55% water). Self-adhering flowable resin was applied to dentin in all groups. Half of the specimens were stored in water for 24 h while the other half underwent 3000 thermal cycles. Later, all specimens received a shear bond strength test. Fracture observation was done first under a stereomicroscope then by using a scanning electron microscope. (3) Results: The mean values of shear bond strength for both laser-treated dentin groups (Er:YAG laser: 13.10 ± 1.291, and Er,Cr:YSGG: 14.04 ± 5.233) were higher than in the control group 1 (8.355 ± 2.297) before thermocycling. After thermocycling, shear bond strength decreased in all groups as follows: 10.03 ± 1.503, 10.53 ± 2.631, and 02.75 ± 1.583 for Er:YAG, Er,Cr:YSGG, and nonirradiated dentin, respectively. Shear bond strength values showed a significant difference between the control group (Group 1) and both lasers groups (Group 2 and 3). Statistical analysis of stereomicroscope observation revealed no significant difference between laser irradiation and failure mode (p < 0.136). SEM observation of the dentin surface in both laser-irradiated groups showed opened tubules, absence of smear layer as well as an increase of resin infiltration into dentinal tubules. (4) Conclusion: Er:YAG and Er,Cr:YSGG lasers enhance self-adhering flowable resin shear bond strength values and improve its longevity by eliminating the smear layer, opening dentinal tubules and increasing resin infiltration into the microstructure.