Crystalline zinc tin oxide (ZTO; zinc oxide with heavy tin doping of 33 at.%) nanowires were first synthesized using the electrodeposition and heat treatment method based on an anodic aluminum oxide (AAO) membrane, which has an average diameter of about 60 nm. According to the field emission scanning electron microscopy (FE-SEM) results, the synthesized ZTO nanowires are highly ordered and have high wire packing densities. The length of ZTO nanowires is about 4 μm, and the aspect ratio is around 67. ZTO nanowires with a Zn/(Zn + Sn) atomic ratio of 0.67 (approximately 2/3) were observed from an energy dispersive spectrometer (EDS). X-ray diffraction (XRD) and corresponding selected area electron diffraction (SAED) patterns demonstrated that the ZTO nanowire is hexagonal single-crystalline. The study of ultraviolet/visible/near-infrared (UV/Vis/NIR) absorption showed that the ZTO nanowire is a wide-band semiconductor with a band gap energy of 3.7 eV.

Stannous oxide (SnO) nanowires were synthesized by a template and catalyst-free thermal oxidation process. After annealing a Sn nanowires-embedded anodic aluminum oxide (AAO) template in air, we obtained a large amount of SnO nanowires. SnO nanowires were first prepared by electrochemical deposition and an oxidization method based on an AAO template. The preparation of SnO nanowires used aluminum sheet (purity 99.999%) and then a two-step anodization procedure to obtain a raw alumina mold. Finally, transparent alumina molds (AAO template) were obtained by reaming, soaking with phosphoric acid for 20 min, and a stripping process. We got a pore size of < 20 nm on the transparent alumina mold. In order to meet electroplating needs, we produced a platinum film on the bottom surface of the AAO template by using a sputtering method as the electrode of electroplating deposition. The structure was characterized by X-ray diffraction (XRD). High resolution transmission electron microscopy (HRTEM) and field emission scanning electron microscopy (FESEM) with X-ray energy dispersive spectrometer (EDS) were used to observe the morphology. The EDS spectrum showed that components of the materials were Sn and O. FE-SEM results showed the synthesized SnO nanowires have an approximate length of ~10–20 μm with a highly aspect ratio of > 500. SnO nanowires with a Sn/O atomic ratio of ~1:1 were observed from EDS. The crystal structure of SnO nanowires showed that all the peaks within the spectrum lead to SnO with a tetragonal structure. This study may lead to the use of the 1D structure nanowires into electronic nanodevices and/or sensors, thus leading to nano-based functional structures.

In this study, alpha nickel sulfide (α-NiS) nanosphere films have been successfully synthesized by electroplating the nickel nanosheet film on the indium tin oxide (ITO) glass substrate and sulfuring nickel-coated ITO glass substrate. First, we electrodeposited the nickel nanosheet films on the ITO glass substrates which were cut into a 0.5 × 1 cm2 size. Second, the nanosheet nickel films were annealed in vacuum-sealed glass ampoules with sulfur sheets at different annealing temperatures (300, 400, and 500 °C) for 4 h in vacuum-sealed glass ampoules. The α-NiS films were investigated by using X-ray diffraction (XRD), variable vacuum scanning electron microscopy (VVSEM), field emission scanning electron microscopy/energy dispersive spectrometer (FE-SEM/EDS), cyclic voltammogram (CV), electrochemical impedance spectroscopy (EIS), ultraviolet/visible/near-infrared (UV/Visible/NIR) spectra, and photoluminescence (PL) spectra. Many nanospheres were observed on the surface of the α-NiS films at the annealing temperature 400 °C for 4 h. We also used the high-resolution transmission electron microscopy (HR-TEM) for the analysis of the α-NiS nanospheres. We demonstrated that our α-NiS nanosphere film had a linear current response to different glucose concentrations. Additionally, our α-NiS nanosphere films were preserved at room temperature for five and a half years and were still useful for detecting glucose at low concentration.

This work investigates a simple and non-toxic method to transform pre-deposited amorphous Co film into CoSe₂ films at a fixed, low temperature of 300 °C. Single CoSe₂-phase films having good crystallinity were obtained at a selenisation time 24 hours. A nanostructure CoSe2 having two different nano-morphological layers was observed. The CoSe₂ films (72 hours) observed a large absorption and a direct band gap.

The β-nickel sulfide (β-NiS) nanobelts were fabricated by electrodepositing a nickel nanosheet film on Indium tin oxide (ITO)-coated glass substrates and sulfuring the nickel film on ITO-coated glass substrates. The sulfurization method can be used to form nanobelts without a template. A small glass tube was used to anneal the sulfur sheet with a nickel nanosheet film. After applying vacuum to the tube, the specimen was annealed at 500 °C. By adjusting the weight of the sulfur sheet in a small glass tube, a nanobelt structure can be formed on the film for 4 h. The β-NiS nanobelt film had a sulfide and nickel molar ratio that was nearly 0.7 (S/Ni). After five years of a long-term storage test, the β-NiS nanobelt films were able to measure the glucose in a solution with the value of sensitivity of 8.67 µA cm⁻² µM⁻¹. The β-NiS nanobelt film also detected glucose with a limit of low detection (LOD) of around 0.173 µM. The estimation of reproducibility was over 98%. Therefore, the β-NiS nanobelt film has a significant ability to detect low concentrations of glucose in a solution.