The penetration resistance of the new material Basic Magnesium Sulfate Cement (BMSC) is studied through comprehensive application of an experimental and numerical simulation method. This paper consists of three parts. The first part introduces the preparation of Basic Magnesium Sulfate Cement Concrete (BMSCC) and the study of its dynamic mechanical properties. In the second part, on-site testing was carried out on both BMSCC and an ordinary Portland cement concrete (OPCC) target, and the anti-penetration performance of the two materials was analyzed and compared from three aspects: penetration depth, crater diameter and volume, and failure mode. In the last part, the numerical simulation analysis was carried out based on LS-DYNA, and the effects of factors, such as material strength and penetration velocity on the penetration depth, are analyzed. According to the results, the BMSCC targets have better penetration resistance performance than OPCC under the same conditions, mainly manifested in smaller penetration depth, smaller crater diameter and volume, as well as fewer cracks.

This study presents a comprehensive investigation into the mechanical properties of Basic Magnesium Sulfate Cement Concrete (BMSC) in comparison to Ordinary Portland Cement Concrete (OPC) within reinforced concrete components. The main objective is to evaluate BMSC’s applicability for practical engineering purposes, with a focus on its with early high strength, improved toughness, and superior crack resistance compared to conventional concrete. Experimental procedures involved fabricating beam specimens using OPC concrete with a C40 strength grade, alongside BMSC beams with varying strength grades (C30, C40, and C50). These specimens underwent bending resistance tests to analyze crack patterns and mechanical characteristics. The findings reveal that BMSC beams demonstrate enhanced bending and tensile properties at equivalent strength grades compared to OPC beams. Particularly, cracking mainly occurred at the mid-span region of BMSC beams, characterized by narrower cracks, indicating superior crack resistance. However, it was noted that the toughness of BMSC beams decreases as the strength grade increases. The maximum mid-span deflection of the BMSC test beam was smaller than that of the OPC test beam, which was 3.8 mm and 2.6 mm, respectively. The maximum crack width of the OPC beam was 4.7 times that of the BMSC beam. To facilitate practical implementation, the study developed calculation models for estimating the crack bending distance and ultimate bending distance in BMSC beams, offering valuable tools for engineering design and optimization. Overall, this research provides significant insights into the mechanical behavior of BMSC, presenting potential advantages for structural engineering applications.