In regions characterized by the challenging combination of brine corrosion in the salt lakes and river sand with alkali silica reaction (ASR) activity in areas of the Northwest, high-performance concrete (HPC) formulated with high-volume composite mineral admixtures as ASR suppression measures has been preferred for civil engineering structures in the region. This study investigates the splitting tensile strength, corrosion products, microscopic structure characteristics, and mesoscopic mechanical mechanisms of splitting failure of such HPC under 10-year corrosion from salt lake brine. The relationship between mechanical properties and corrosion damage, as well as the characteristics of internal crack propagation paths and failure mechanisms of HPC under splitting load, are explored. The findings reveal that as the alkali content within HPC rises, corrosion damage intensifies, resulting in a reduction in splitting tensile strength. Moreover, a linear association between mechanical properties and corrosion damage is observed. Microscopic structural analysis and numerical simulation of the splitting failure process of HPC elucidate that while the substantial presence of mineral admixtures effectively suppresses the ASR risk associated with alkali-reactive aggregates in concrete, uneven ASR gel products persist. These discontinuous micro-fine interface cracks induced by the gel products and the cracks induced by the gel products around the selective alkali-active aggregate particles distributed in the local area are the initiation sources of mortar cracks in HPC splitting failure. In terms of the overall failure state observed during the concrete splitting process, mortar cracks manifest two distinct extension paths: along the coarse aggregate interface and directly through the aggregates themselves. Notably, a greater proportion of coarse aggregates are directly penetrated by mortar cracks, as opposed to the number of interface failures bypassing coarse aggregates. More importantly, the above work establishes a theoretical reference in three dimensions: macroscopic, mesoscopic, and microscopic, for studying concrete corrosion damage in complex environments such as salt lake brine corrosion and ASR inhibition.

This paper comprehensively investigates the dynamic mechanical properties of concrete by employing a 75 mm diameter Split Hopkinson Pressure Bar (SHPB). To be detailed further, dynamic compression experiments are conducted on coral aggregate seawater concrete (CASC) to unveil the relationship between the toughness ratio, strain rate, and different strength grades. A three-dimensional random convex polyhedral aggregate mesoscopic model is also utilized to simulate the damage modes of concrete and its components under varying strain rates. Additionally, the impact of different aggregate volume rates on the damage modes of CASC is also studied. The results show that strain rate has a significant effect on CASC, and the strength grade influences both the damage mode and toughness index of the concrete. The growth rate of the toughness index exhibits a distinct change when the 28-day compressive strength of CASC ranges between 60 and 80 MPa, with three times an increment in the toughness index of high-strength CASC comparing to low-strength CASC undergoing high strain. The introduction of pre-peak and post-peak toughness highlights the lowest pre-to-post-peak toughness ratio at a strain rate of approximately 80 s⁻¹, which indicates a shift in the concrete’s damage mode. Various damage modes of CASC are under dynamic impact and are consequently defined based on these findings. The LS-DYNA finite element software is employed to analyze the damage morphology of CASC at different strain rates, and the numerical simulation results align with the experimental observations. By comparing the numerical simulation results of different models with varying aggregate volume rates, it is reported that CASC’s failure mode is minimized at an aggregate volume rate of 20%.

This study presents a comprehensive investigation into the mechanical properties of Basic Magnesium Sulfate Cement Concrete (BMSC) in comparison to Ordinary Portland Cement Concrete (OPC) within reinforced concrete components. The main objective is to evaluate BMSC’s applicability for practical engineering purposes, with a focus on its with early high strength, improved toughness, and superior crack resistance compared to conventional concrete. Experimental procedures involved fabricating beam specimens using OPC concrete with a C40 strength grade, alongside BMSC beams with varying strength grades (C30, C40, and C50). These specimens underwent bending resistance tests to analyze crack patterns and mechanical characteristics. The findings reveal that BMSC beams demonstrate enhanced bending and tensile properties at equivalent strength grades compared to OPC beams. Particularly, cracking mainly occurred at the mid-span region of BMSC beams, characterized by narrower cracks, indicating superior crack resistance. However, it was noted that the toughness of BMSC beams decreases as the strength grade increases. The maximum mid-span deflection of the BMSC test beam was smaller than that of the OPC test beam, which was 3.8 mm and 2.6 mm, respectively. The maximum crack width of the OPC beam was 4.7 times that of the BMSC beam. To facilitate practical implementation, the study developed calculation models for estimating the crack bending distance and ultimate bending distance in BMSC beams, offering valuable tools for engineering design and optimization. Overall, this research provides significant insights into the mechanical behavior of BMSC, presenting potential advantages for structural engineering applications.

The natural environment in the high-altitude regions of Northwest China is extremely harsh, characterized by numerous salt lakes. The high concentrations of chloride salts, sulfates, and alkali metal ions in these areas can induce alkali–silica reactions (ASRs) in concrete. These reactions generate harmful gel within the concrete, causing expansion and cracking, which significantly impacts the durability of concrete structures. This study investigates the evolution of the mechanical properties in high-performance concrete (HPC) under long-term ASR by incorporating different admixtures and varying the equivalent alkali content. A three-dimensional random aggregate mesoscopic model was used to simulate static compression tests under various operational conditions. Non-destructive testing methods were utilized to determine the expansion rate, internal, and surface damage variables of the concrete. The experimental results indicate that the 10-year expansion rate differs from the 1-year rate by approximately 1%, and under long-term ASR mitigation measures, the internal damage in the HPC is minimal, though the surface damage is more severe. As the equivalent alkali content increases, the compressive strength of the concrete cubes decreases, initially rising before falling by 5–15% over time. The HPC with only air-entraining agent added exhibited better mechanical performance than the HPC with both air-entraining and corrosion inhibitors added, with the poorest performance observed in the HPC with only a corrosion inhibitor. A relationship was established between the surface and internal damage variables, with the surface damage initially increasing rapidly before stabilizing as the internal damage rose. Numerical simulations effectively describe the damage behavior of HPC under static uniaxial compression. Comparisons with actual failure morphologies revealed that, in the cube compression tests, crack propagation directly penetrated both coarse and fine aggregates rather than circumventing them. The simulations closely matched the experimental outcomes, demonstrating their accuracy in modeling experiments. This study discusses the compressive mechanical properties of concrete under prolonged ASR through a combination of experimental and simulation approaches. It also delves into the impact of surface damage on the overall mechanical performance and failure modes of concrete. The findings provide experimental and simulation support for the concrete structures in regions with high alkali contents.