In this work, the influence of the Sargassum natans I alga extract on the morphological characteristics of synthesized ZnO nanostructures, with potential biological and environmental applications, was evaluated. For this purpose, different ZnO geometries were synthesized by the co-precipitation method, using Sargassum natans I alga extract as stabilizing agent. Four extract volumes (5, 10, 20, and 50 mL) were evaluated to obtain the different nanostructures. Moreover, a sample by chemical synthesis, without the addition of extract, was prepared. The characterization of the ZnO samples was carried out by UV-Vis spectroscopy, FT-IR spectroscopy, X-ray diffraction, and scanning electron microscopy. The results showed that the Sargassum alga extract has a fundamental role in the stabilization process of the ZnO nanoparticles. In addition, it was shown that the increase in the Sargassum alga extract leads to preferential growth and arrangement, obtaining well-defined shaped particles. ZnO nanostructures demonstrated significant anti-inflammatory response by the in vitro egg albumin protein denaturation for biological purposes. Additionally, quantitative antibacterial analysis (AA) showed that the ZnO nanostructures synthesized with 10 and 20 mL of extract demonstrated high AA against Gram (+) S. aureus and moderate AA behavior against Gram (-) P. aeruginosa, depending on the ZnO arrangement induced by the Sargassum natans I alga extract and the nanoparticles’ concentration (ca. 3200 µg/mL). Additionally, ZnO samples were evaluated as photocatalytic materials through the degradation of organic dyes. Complete degradation of both methyl violet and malachite green were achieved using the ZnO sample synthesized with 50 mL of extract. In all cases, the well-defined morphology of ZnO induced by the Sargassum natans I alga extract played a key role in the combined biological/environmental performance.

Currently, the ethanol electro-oxidation reaction has attracted considerable attention in fuel cells because of new green ethanol synthetic methods based on biomass processes that have emerged. In this study, PtFe/C and Pt/C nanoparticles were synthesized by a chemical reduction method and tested in the ethanol electro-oxidation reaction. Furthermore, the electrocatalytic effect of the PtFe bimetallic catalyst was analyzed by in situ surface-enhanced Raman spectroscopy (SERS) coupled to an electrochemical cell. X-ray diffractograms showed typical face-centered cubic structures with crystallite sizes of 3.31 and 3.94 for Pt/C and PtFe/C, respectively. TEM micrographs revealed nanoparticle sizes of 2 ± 0.4 nm and 3 ± 0.6 nm for Pt/C and PtFe/C respectively. PtFe/C exhibited a Pt₉₀Fe₁₀ composition by both X-ray fluorescence and energy-dispersive X-ray spectroscopy. A better electrocatalytic activity as function of concentration was obtained through the incorporation of a small amount of Fe into the Pt lattice and the presence of Fe²⁺/Fe³⁺ (observed by X-ray photoelectron spectroscopy). According to SERS experiments, the presence of these iron species promotes the chemisorption of ethanol, the formation of formic acid as main product and renewal of the catalytic sites, resulting in current densities that were at least three fold higher than the values obtained for the Pt/C nanocatalyst.